Rubber composition

ABSTRACT

A rubber composition comprising a vulcanizable rubber, a reinforcing filler, a softening agent, and other reagents for rubber to which is added in a specific amount of a sulfur compound having the formula (I):  
     —(S x R 1 ) n —  (I)  
     wherein R 1  represents an organic group, x is a number of 3 to 5 on average, and n is an integer of 1 to 100, or a specific sulfur compound (1) and sulfur (2), and  
     optionally a thiazole base, sulfenamide base, thiuram base, and/or diothio acid base vulcanization accelerator (3).

BACKGROUND OF THE INVENTION

[0001] 1. Field of the Invention

[0002] The present invention relates to a vulcanized rubber composition, more particularly relates to a vulcanized rubber composition balanced in heat aging characteristics, fatigue resistance, and heat buildup property by using a sulfur compound having a specific structure and optionally sulfur, to control the sulfur cross-linking structure of the rubber.

[0003] The present invention also relates to a rubber composition for a heavy duty tire tread, more particularly relates to a rubber composition for a heavy duty tire tread in which a diene rubber is compounded with a reinforcing filler, rosin base and/or cyclopentadiene base resin, sulfur compound having a specific tetrasulfide or benzothiazole structure so as to improve the abrasion resistance, heat aging characteristics, and appearance after use while maintaining the heat buildup properly of the tire and the cut resistance when new.

[0004] 2. Description of the Related Art

[0005] In the past, mainly sulfur has been used as a vulcanization agent for vulcanization of rubber, but rubber compositions comprising blends of rubber compositions with polysulfide polymers are known. For example, Japanese Unexamined Patent Publication (Kokai) No. 10-120788 describes a polysulfide polymer used as a rubber vulcanization agent, Japanese Unexamined Patent Publication (Kokai) No. 10-139939 describes a cross-linkable rubber composition containing a polysulfide rubber, and Japanese Unexamined Patent Publication (Kokai) No. 10-251514 also describes a rubber composition containing a polysulfide polymer. Further, Japanese Unexamined Patent Publication (Kokai) No. 62-48739 describes a high grip tread rubber composition suitable for high speed driving.

[0006] The sulfur cross-linking structures of rubber are roughly classified into monosulfide bridges, disulfide bridges, and polysulfide bridges, but in general it is said that the greater the monosulfide bridges in vulcanized rubber, the better the heat aging characteristics become. If there are many monosulfide bridges, however, there is the problem that the strength and elongation at break and the fatigue failure characteristics fall. On the other hand, if there are many polysulfide bridges in the vulcanized rubber, while the strength and elongation at break and the fatigue failure characteristics are superior, there is the problem that the heat aging characteristics fall.

[0007] In addition, a general diene-base rubber suffers from the phenomenon of reversion where the various physical properties fall upon high temperature vulcanization in the case of a sulfur/vulcanization accelerator vulcanization system. Improvement of this is sought. To improve this, it is desirable to add a polysulfide polymer having 2 to 5 sulfur atoms, but there is the problem that if this is not suitably blended in, it causes a remarkable change in other physical properties and in particular causes a deterioration of the heat buildup property.

[0008] Furthermore, in heavy duty tires such as tires for construction machinery which are used on bad roads and under heavy duty conditions, improvement in the heat buildup property, the abrasion resistance, and other properties is sought. At the same time, in recent years, there have been rising demands for prevention of a decline in physical properties due to use and securing a good appearance due to the same. In order to meet these demands, for example, Japanese Unexamined Patent Publication (Kokai) No. 10-219034 proposes a specific ratio of formulation of specific carbon black and silica. Further, from the same viewpoint as the present invention, in the sense of prevention of heat degradation, it has been proposed to use a sulfur compound such as polyalkylene tetrasulfide (condensed product of sodium tetrasulfide and an alkylene dihalide) in order to obtain a thermally stable cross-linking state (see 1967 Synthetic Rubber Handbook (enlarged new edition), p. 309), but control of the molecular weight for securing the compatibility with rubber and handling is difficult and this is not preferred from the viewpoints of scorch resistance and safety.

SUMMARY OF THE INVENTION

[0009] Therefore, an object of the present invention is to provide a vulcanized rubber composition balanced in heat aging characteristics, fatigue resistance, and heat buildup property.

[0010] Another object of the present invention is to provide a vulcanized rubber composition improved in reversion resistance without changing the other physical properties.

[0011] A further object of the present invention is to provide a rubber composition for a heavy duty tire tread which enables improvement of the abrasion resistance, heat aging characteristics, and appearance after use while maintaining the heat buildup property, cut resistance when new, and other properties.

[0012] Other objects and advantages of the present invention will be apparent from the following description.

[0013] In accordance with the first aspect of the present invention, there is provided a vulcanized rubber composition comprising a vulcanizable rubber, a reinforcing filler, and a sulfur compound (1) having the formula (I):

—(S_(x)R¹)_(n)—  (I)

[0014] wherein R¹ represents an organic group, x is an average number of 3 to 5, and n is an integer of 1 to 100, wherein a ratio (VM/VD) is not more than 0.4, in which:

[0015] a value VM is obtained from the degree of change before and after toluene swelling of the vulcanized rubber composition treated in a lithium aluminum hydride saturated tetrahydrofuran/toluene (ratio by volume 1/1) mixed solution using the formula (A): $\begin{matrix} {{{VM} = {{{- \frac{1}{Vs}} \cdot \left\lbrack \frac{{{\ln \left( {1 - {vr}_{M}} \right)} + {vr}_{M} + \mu}{\cdot {vr}_{M}^{2}}}{{vr}_{M}^{1/3} - {{vr}_{M}/2}} \right\rbrack}\quad {wherein}}}{{vr}_{M} = \frac{1 - \varphi}{X_{M} - \varphi}}} & (A) \end{matrix}$

[0016] wherein X_(M) is the degree of change before and after toluene swelling (volume after toluene swelling/volume before toluene swelling)after treatment in a lithium aluminum hydride saturated tetrahydrofuran/toluene (ratio by volume 1/1) mixed solution,

[0017] φ is the volume percentage of the reinforcing filler in the rubber composition,

[0018] V_(s) is the molecular volume of toluene,

[0019] μ is the rubber•toluene interaction coefficient, and

[0020] vr_(M) is the volume percentage of rubber in the swelled rubber after treatment in a lithium aluminum hydride saturated tetrahydrofuran/toluene (ratio by volume 1/1) mixed solution and

[0021] a value VD is obtained from the degree of change before and after toluene swelling of the vulcanized rubber composition treated in a propane-2-thiol (0.4 mol/l)/piperidine (0.4 mol/l) added tetrahydrofuran/toluene (ratio by volume 1/1) mixed solution using the formula (B): $\begin{matrix} \begin{matrix} {{VD} = {{- \frac{1}{Vs}} \cdot \left\lbrack {\frac{{\ln \left( {1 - {vr}_{D + M}} \right)} + {vr}_{D + M} + {\mu \cdot {vr}_{D + M}^{2}}}{{vr}_{D + M}^{1/3} - {{vr}_{D + M}/2}} -} \right.}} \\ {{\left. \frac{\left. {{\ln \left( {1 - {vr}_{M}} \right)} + {vr}_{M}} \right) + {\mu \cdot {vr}_{M}^{2}}}{{vr}_{M}^{1/3} - {{vr}_{M}/2}} \right\rbrack}\quad {wherein}} \\ {{{vr}_{D + M} = \frac{1 - \varphi}{x_{D + M} - \varphi}}} \end{matrix} & (B) \end{matrix}$

[0022] wherein X_(D+M) is the degree of change before and after toluene swelling (volume after toluene swelling/volume before toluene swelling)after treatment in a propane-2-thiol (0.4 mol/l)/piperidine (0.4 mol/l) added tetrahydrofuran/toluene (ratio by volume 1/1) mixed solution and

[0023] vr_(D+M) is the volume percentage of rubber in the swelled rubber after treatment in a propane-2-thiol (0.4 mol/l)/piperidine (0.4 mol/l) added tetrahydrofuran/toluene (ratio by volume 1/1) mixed solution).

[0024] A vulcanized rubber composition according to the preferable embodiment of the first aspect of the present invention further has a ratio (VM/VT) is not more than 0.15, in which:

[0025] VT found from the degree of change before and after toluene swelling of the untreated vulcanized rubber composition using formula (C): $\begin{matrix} {{{VT} = {{{- \frac{1}{Vs}} \cdot \left\lbrack \frac{{\ln \left( {1 - {vr}_{T}} \right)} + {vr}_{T} + {\mu \cdot {vr}_{T}^{2}}}{{vr}_{T}^{1/3} - {{vr}_{T}/2}} \right\rbrack}\quad {wherein}}}{{vr}_{T} = \frac{1 - \varphi}{X_{T} - \varphi}}} & (C) \end{matrix}$

[0026] where X_(T) is the degree of change before and after toluene swelling when untreated (volume after toluene-swelling/volume before toluene swelling) and vr_(T) is the volume percentage of rubber in the swelled rubber when untreated and

[0027] VM is defined above.

[0028] In accordance with the second aspect of the present invention, there is also provided a vulcanized rubber composition comprising 100 parts by weight of a vulcanizable rubber, a reinforcing filler, and a sulfur compound (1) having the formula (I):

(S_(x)R¹)_(n)—  (I)

[0029] wherein R¹ represents an organic group, x is an average number of 3 to 5, and n is an integer of 1 to 100 in an amount of not more than 20 parts by weight or the sulfur compound (1)

[0030] and sulfur (2) in a ratio by weight (1)/(2) of at least 0.5 and in a total weight of (1)+(2) of not more than 20 parts by weight, vulcanized by compounding at least one vulcanization accelerator (3) selected from the group consisting of a thiazole base, sulfenamide base, thiuram base, and diothio acid base accelerator in an amount so as to give a ratio by weight [(1)+(2)]/(3) of not more than 2.2, wherein

[0031] a value VM is obtained from the degree of change before and after toluene swelling of the vulcanized rubber composition treated in a lithium aluminum hydride saturated tetrahydrofuran/toluene (ratio by volume 1/1) mixed solution using the formula (A): $\begin{matrix} {{{VM} = {{{- \frac{1}{Vs}} \cdot \left\lbrack \frac{{{\ln \left( {1 - {vr}_{M}} \right)} + {vr}_{M} + \mu}{\cdot {vr}_{M}^{2}}}{{vr}_{M}^{1/3} - {{vr}_{M}/2}} \right\rbrack}\quad {wherein}}}{{vr}_{M} = \frac{1 - \varphi}{X_{M} - \varphi}}} & (A) \end{matrix}$

[0032] wherein X_(M) is the degree of change before and after toluene swelling (volume after toluene swelling/volume before toluene swelling)after treatment in a lithium aluminum hydride saturated tetrahydrofuran/toluene (ratio by volume 1/1) mixed solution,

[0033] φ is the volume percentage of the reinforcing filler in the rubber composition,

[0034] V_(s) is the molecular volume of toluene,

[0035] μ is the rubber•toluene interaction coefficient, and

[0036] vr_(M) is the volume percentage of rubber in the swelled rubber after treatment in a lithium aluminum hydride saturated tetrahydrofuran/toluene (ratio by volume 1/1) mixed solution,

[0037] a value V[D+M] is obtained from the degree of change before and after toluene swelling of the vulcanized rubber composition treated in a propane-2-thiol (0.4 mol/l)/piperidine (0.4 mol/l) added tetrahydrofuran/toluene (ratio by volume 1/1) mixed solution using the formula (D): $\begin{matrix} {{{V\left\lbrack {D + M} \right\rbrack} = {{- \frac{1}{Vs}} \cdot \left\lbrack \frac{{\ln \left( {1 - {vr}_{D + M}} \right)} + {vr}_{D + M} + {\mu \cdot {vr}_{D + M}^{2}}}{{vr}_{D + M}^{1/3} - {{vr}_{D + M}/2}} \right\rbrack}}{{{wherein}\quad {vr}_{D + M}} = \frac{1 - \varphi}{X_{D + M} - \varphi}}} & (D) \end{matrix}$

[0038] wherein X_(D+M) is the degree of change before and after toluene swelling (volume after toluene swelling/volume before toluene swelling)after treatment in a propane-2-thiol (0.4 mol/l)/piperidine (0.4 mol/1) added tetrahydrofuran/toluene (ratio by volume 1/1) mixed solution, φ, Vs, μ, and vr_(M) are as defined above, and vr_(D+M) is the volume percentage of rubber in the swelled rubber after treatment in a propane-2-thiol (0.4 mol/l)/piperidine (0.4 mol/l) added tetrahydrofuran/toluene (ratio by volume 1/1) mixed solution), and

[0039] a value VT is obtained from the degree of change before and after toluene swelling of the untreated vulcanized rubber composition using formula (C): $\begin{matrix} {{{VT} = {{{- \frac{1}{Vs}} \cdot \left\lbrack \frac{{\ln \left( {1 - {vr}_{T}} \right)} + {vr}_{T} + {\mu \cdot {vr}_{T}^{2}}}{{vr}_{T}^{1/3} - {{vr}_{T}/2}} \right\rbrack}\quad {wherein}}}{{vr}_{T} = \frac{1 - \varphi}{X_{T} - \varphi}}} & (C) \end{matrix}$

[0040] wherein X_(T) is the degree of change before and after toluene swelling when untreated (volume after toluene swelling/volume before toluene swelling) and vr_(T) is the volume percentage of rubber in the swelled rubber when untreated

[0041] are such that VM/VT is not more than 0.3 and (VT−V[D+M])/VT is at least 0.4 and further are such that the ratio VM/VD of VD(=V[D+M]−VM) and VM is at least 0.4 and wherein

[0042] the rate of retention of the tensile strength at break and the elongation at break of the vulcanized rubber composition before and after heat aging at 100° C. for 96 hours is at least 0.7.

[0043] In accordance with the third aspect of the present invention, there is further provided a rubber composition comprising 100 parts by weight of a vulcanizable rubber, a reinforcing filler, and a sulfur compound (1) having the formula (I):

—(S_(x)R¹)_(n)—  (I)

[0044] wherein R¹ represents an organic group,

[0045] x is an average number of 3 to 5, and

[0046] n is an integer of 1 to 100

[0047] and sulfur (2), in a ratio (1)/(2) of the sulfur compound (1) and the sulfur (2) of less than 0.5 and in a total weight of (1)+(2) of not more than 20 parts by weight.

[0048] In accordance with the fourth aspect of the present invention, there is still further provided a rubber composition for a heavy duty tire tread comprising 100 parts by weight of a diene rubber, 40 to 85 parts by weight of a reinforcing filler, 1 to 10 parts by weight of at least one resin selected from the group consisting of a rosin base resin, a cyclopentane diene base resin, and mixtures thereof, a sulfur compound having the formula (I) or (II):

—(S_(x)R¹)_(n)—  (I)

[0049] wherein R¹ indicates an organic group,

[0050] x is an integer of 3 to 5, and

[0051] n is an integer of 1 to 100

[0052] wherein n is an integer of 3 or 4

[0053] and, in some cases, sulfur or a sulfur donor.

DESCRIPTION OF THE PREFERRED EMBODIMENTS

[0054] The present inventors engaged in research to achieve the above object and, as a result, succeeded in obtaining a rubber composition achieving both good heat aging characteristics and failure characteristics by using a sulfur compound having a specific structure to control the sulfur cross-linking structure of the rubber. That is, the present inventors took note of an organic polysulfide polymer having a tetrasulfide structure of four sulfur atoms for achieving both good heat aging characteristics and failure characteristics and discovered that by controlling the cross-linking structure together with this, it is possible to achieve both good heat aging characteristics and failure characteristics and heat generation.

[0055] As the cross-linking structure in the first aspect of the present invention, specifically the disulfide bridges are made at least 2.5 times the monosulfide bridges, more preferably the ratio of the monosulfide bridges causing deterioration of the failure characteristics is made not more than 15% of the whole. Further, in the present invention, since a specific organic polysulfide polymer having a tetrasulfide structure is used, even in the case of a polysulfide bridge of three or more sulfur atoms, while it may have as much as eight ordinary sulfur atoms, the number of sulfur bonds is kept down to not more than 4, and therefore, the heat aging characteristics are improved. Further, the sulfur compound of the present invention can greatly shorten the vulcanization time compared with known polysulfide polymer. As the means for obtaining this cross-linking structure, combination with a vulcanization accelerator is best. It is preferable to compound at least one vulcanization accelerator selected from a sulfenamide base, thiazole base, thiuram base, and dithio acid salt base accelerator to give a ratio by weight with the polysulfide polymer of preferably 0.3 to 4, and more preferably 0.3 to 3 and further to compound, into the above combination of the vulcanization accelerator at least one vulcanization accelerator selected from a guanidine base, aldehyde-ammonia base, aldehyde-amine base, and thiourea base accelerator to 0.1 to 1 part by weight.

[0056] As explained above, the vulcanized rubber composition according to the present invention is a rubber composition containing a vulcanizable rubber, a reinforcing filler, and a sulfur compound (1) of the formula (I) which is vulcanized, where the ratio (VM/VD) of the value VM found from the degree of change before and after toluene swelling of the vulcanized rubber composition treated in a lithium aluminum hydride saturated tetrahydrofuran/toluene (ratio by volume 1/1) mixed solution using the formula (A) and the value VD found from the degree of change before and after toluene swelling of the vulcanized rubber composition treated in a propane-2-thiol (0.4 mol/l)/piperidine (0.4 mol/l) added tetrahydrofuran/toluene (ratio by volume 1/1) mixed solution using the formula (B) is not more than 0.4, more preferably where the ratio (VM/VT) of VT found from the degree of change before and after toluene swelling of the untreated vulcanized rubber composition using formula (C) and VM is not more than 0.3, more preferably not more than 0.15.

[0057] The formulas (A), (B), and (C) are generally known as Flory-Rehner formulas for finding the cross-linking density of vulcanized rubber from the swelling degree (ratio of change of volume of a vulcanized rubber before and after immersion in a good solvent). Details of these are given in P. J. Flory, J. Rehner, Journal of Chemical Physics, 11, 521 (1943). As a good solvent for causing swelling of rubber, benzene, toluene, n-hexane, acetone, ethanol, etc. may be mentioned, but in particular toluene is generally used. The μ in the formula, that is, the rubber-toluene interaction coefficient, is determined by the type of the rubber. In the case of natural rubber and isoprene rubber, μ=0.41 (room temperature), in the case of a styrene-butadiene copolymer rubber, μ=0.36 (room temperature, and in the case of a butadiene rubber, μ=0.32 is appropriate.

[0058] As the means for analyzing the sulfur cross-linking structure of vulcanized rubber, the general practice is to analyze the sulfur cross-linking structures by selectively cleaving the sulfur bridges in vulcanized rubber by a reagent and finding the change in volume before and after swelling of the vulcanized rubber after the cleaving reactions, that is, finding the bridge density from the swell using the Flory-Rehner formulas. Details on this are given in A. Y. Coran, Rubber Chemistry and Technology, 37, 668 (1964). This is widely accepted. Further, correction for ingredients which do not swell such as the reinforcing filler etc. blended in is possible in accordance with G. Kraus, Rubber Chemistry and Technology, 31, 6 (1964).

[0059] Regarding the reagents for cleaving the sulfur bridges, as described in L. Bateman and R. W. Glazebrook, Journal of Chemical Society, 2838, 2846 (1958); M. L. Studebaker et al., Rubber Chemistry and Technology, 32, 941 (1959); A. Y. Coran, Rubber Chemistry and Technology, 37, 668 (1964); T. H. Kuan, Rubber World, vol. 192, No. 5 (1985); and Nakauchi, Naito, Utsunomiya, Masuda, and Inoue, Journal of the Japan Rubber Association, vol. 60, No. 5, 267 (1987), to cleave a polysulfide bridge with three or more sulfur atoms, a reagent comprising a combination of a thiol base compound and an amine base compound is preferable. Widely known is a combination of propane-2-thiol and piperidine. To cleave a disulfide and polysulfide bridge, lithium aluminum hydride is most generally used.

[0060] The present inventors performed the cleaving reaction in accordance with Nakauchi, Naito, Utsunomiya, Masuda, and Inoue, Journal of the Japan Rubber Association, vol. 60, No. 5, 267 (1987).

[0061] Here, the VT obtained from the toluene swell of vulcanized rubber not treated for a cleaving reaction using formula (C) is the measure of the overall bridge density. The VM obtained from the toluene swell of the vulcanized rubber treated by lithium aluminum hydride using formula (A) is the measure of the monosulfide bridge density. Therefore, the VD obtained using formula (B) is the monosulfide+disulfide bridge density minus the monosulfide bridge density, obtained from the toluene swell of vulcanized rubber treated by propane-2-thiol/piperidine, and is the measure of the disulfide bridge density.

[0062] The present inventors calculated the VM/VD and the VM/VT from the values VM, VD, and VT obtained from these formulas.

[0063] A VM/VD of more than 0.4 is not preferable since the disulfide bridge component for achieving both good failure characteristics and fatigue failure characteristics and heat aging characteristics is reduced, the balance is lost, and deterioration of the failure characteristics and the fatigue failure characteristics is induced. Further, a VM/VT of more than 0.15 is not preferable since the increase in the monosulfide bridge component causes deterioration of the failure characteristics and the fatigue failure characteristics.

[0064] As the sulfur compound of the formula (I) used in the present invention, mention may be made of polysulfide polymer having a Mooney viscosity of the material (measured in accordance with JIS K6300 using an L-shaped rotor with preheating at 100° C. for 1 minute and turning the rotor for 4 minutes) of not more than 100, preferably not more than 85, and having a number average molecular weight of 200 to 15000, preferably 1000 to 12000, a polysulfide polymer has the formula (III) to which sulfur is added in the backbone and having y of 3 to 5 on average and z of 3 to 5 on average:

R³S_(z)R²(S_(y)R²)_(m)SzR³  (III)

[0065] wherein R² is a C₂ to C₁₀oxyalkylene group and/or a C₂ to C₁₀ and O₂ to O₁₀ polyoxyalkylene group, R³ is at least one functional group selected from a C₁ to C₃₀ hydrocarbon group, preferably a C₃ to C₂₀ hydrocarbon group (for example, an allyl group, benzyl group, etc.), y is a number of 1 to 6, preferably 1.5 to 3.0, z is a number of 1 to 6, preferably 1.5 to 3.0, and m is an integer of 1 to 50, preferably 5 to 40, which polysulfide polymer has an R² of formula (III) shown by the following formula (IV):

—C₂H₄OC_(m′)H_(2m′)OC₂H₄—  (IV)

[0066] wherein, m′ is an integer of 1 or 2, etc.

[0067] In a preferable embodiment of the vulcanized rubber composition according to the present invention, at least one vulcanization accelerator selected from a thiazole base, sulfenamide base, thiuram base, and dithio acid salt base accelerator is compounded in an amount of 0.5 to 5 parts by weight, preferably 0.5 to 3, of the polysulfide polymer so as to give a ratio by weight of the vulcanization accelerator and the polysulfide polymer of 0.3 to 4, preferably 0.3 to 2.

[0068] As the vulcanization accelerator, it is possible to further compound at least one vulcanization accelerator selected from a guanidine base, aldehyde-ammonia base, aldehyde-amine base, and thiourea base accelerator to 0.05 to 1 part by weight, preferably 0.1 to 0.7 part by weight, based upon 100 parts by weight of the starting rubber.

[0069] Specific examples of the vulcanization accelerators which can be used in the present invention are given below:

[0070] Thiazole-Base Vulcanization Accelerators

[0071] As the thiazole, 2-mercaptobenzothiazole (MBT), dibenzothiazyldisulfide (MBTS), a zinc salt of 2-mercaptobenzothiazole (ZnMBT), a sodium salt of 2-mercaptobenzothiazole (NaMBT), a cyclohexylamine salt of 2-mercaptobenzothiazole (CMBT), and 2-(2,4-dinitrophenylthio)benzothiazole (DPBT) may be mentioned.

[0072] Sulfenamide Base Vulcanization Accelerators

[0073] As the sulfenamide, N-cyclohexyl-2-benzothiazolesulfenamide (CBS), N-t-butyl-2-benzothiazolesulfenamide (TBBS), N-oxyethylene-2-benzothiazolesulfenamide (OBS), and N,N′-diisopropyl-2-benzothiazolesulfenamide (DPBS) may be mentioned.

[0074] Thiuram Base Vulcanization Accelerators

[0075] As the thiuram, tetramethylthiuram monosulfide (TMTM), tetramethylthiuram disulfide (TMTD), tetraethylthiuram disulfide (TETD), tetrabutylthiuram disulfide (TBTD), and dipentamethylenethiuram tetrasulfide (DPTT) may be mentioned.

[0076] Guanidine Base Vulcanization Accelerators

[0077] As the guanidine, diphenylguanidine (DPG), diorthotolylguanidine (DOTG), and orthotolylbiguamide (OTBG) may be mentioned.

[0078] Dithio Acid Salt Base Vulcanization Accelerators

[0079] As the dithio acid salt, sodium dimethyldithiocarbamate (NaMDC), sodium diethyldithiocarbamate (NaEDC), sodium di-n-butyldithiocarbamate (NaBDC), lead dimethyldithiocarbamate (PbMDC), zinc dimethyldithiocarbamate (ZnMDC), zinc diethyldithiocarbamate (ZnEDC), zinc di-n-butyldithiocarbamate (ZnBDC), zinc pentamethylene dithiocarbamate (ZnPDC), zinc ethylphenyldithiocarbamate (ZnEPDC), tellurium diethyldithiocarbamate (TeEDC), selenium dimethyldithiocarbamate (SeMDC), selenium diethyldithiocarbamate (SeEDC), copper dimethyldithiocarbamate (CuMDC), iron dimethyldithiocarbamate (FeMDC), diethylamine diethyldithiocarbamate (EAEDC), piperidine pentamethylenedithiocarbamate (PPDC), and pipecoline methylpentamethylenedithiocarbamate (PMPDC) may be mentioned.

[0080] Thiourea Base Vulcanization Accelerators

[0081] As the thiourea, thiocarboanilide (CA), diorthotolylthiourea (DOTU), ethylenethiourea (EU), diethylthiourea (DEU), and trimethylthiourea (TMU) may be mentioned.

[0082] Aldehyde-Ammonia Base and Aldehyde-Amine Base Vulcanization Accelerators

[0083] As the aldehyde•ammonia, hexamethylenetetramine (H) and acetoaldehyde•ammonia (AA) may be mentioned.

[0084] As the aldehyde•amine, an n-butylaldehyde•aniline reaction product (BAA) may be mentioned.

[0085] As the vulcanizable rubber used in the present invention, for example any vulcanizable rubber generally used in for tire or other rubber applications in the past, specifically natural rubber (NR), butadiene rubber (BR), isoprene rubber (IR), chloroprene rubber (CR), butyl rubber (IIR), various styrene-butadiene rubbers (SBR), and other diene base rubbers or mixtures of the same may be mentioned.

[0086] As the vulcanization agent of the present invention, in addition to the above sulfur compound, sulfur and/or another sulfur donor may be used. As this sulfur, it is possible to use any sulfur being used for vulcanization of ordinary rubber. As the form of the same, sublimated sulfur, precipitated sulfur, flower of sulfur, colloidal sulfur, etc. may be mentioned.

[0087] The compounding ratio of the rubber composition according to the present invention is not particularly limited, but preferably the sulfur compound having the formula (I) is blended in an amount of 0.3 to 3.5 parts by weight, in terms of effective sulfur, based upon, 100 parts by weight of the vulcanizable rubber. If the amount of the sulfur is too small, vulcanization does not occur and sufficient physical properties are not obtained, while conversely if too large, scorching and other poor processability are caused.

[0088] As the reinforcing filler used in the rubber composition according to the present invention, those generally compounded for rubber use in the past, such as carbon black, silica, clay, talc, or surface-treated carbon black may be mentioned. The amount of the reinforcing filler blended in is preferably 40 to 120 parts by weight with respect to 100 parts by weight of the vulcanizable rubber.

[0089] The rubber composition according to the present invention may contain, in addition to the above essential ingredients, other ingredients generally used for blending in rubber such as other fillers, promoters such as zinc oxide and magnesium oxide, waxes, antioxidants, anti ozone crack agents, masticating accelerants, viscous resins, processing oils, and vulcanization retarders. The amounts compounded are within the general ranges unless impairing the object of the present invention.

[0090] As the vulcanization agent of the second aspect of the present invention, in addition to the above sulfur compound (1), sulfur (2) (or another sulfur donor) is used. As this sulfur (2), it is possible to use any sulfur being used for vulcanization of ordinary rubber. As the form of the same, sublimated sulfur, precipitated sulfur, flowers of sulfur, colloidal sulfur, etc. may be mentioned.

[0091] In the vulcanized rubber composition according to the second aspect of the present invention, the sulfur compound (1) of the formula (I) is compounded in an amount of not more than 20 parts by weight, preferably 1 to 10 parts by weight, more preferably 1 to 4 parts by weight, or the sulfur compound (1) and the sulfur (2) are compounded at a ratio of (1)/(2) by weight of not less than 0.5, preferably 0.6 to 0.5, in a total weight of (1)+(2) of not more than 20 parts by weight, preferably 1 to 10 parts by weight, based upon 100 parts by weight of vulcanizable rubber. A ratio (1)/(2) of less than 0.5 is not desirable since the desired cross-linking structure is not obtained and good failure characteristics and fatigue characteristics and heat aging characteristics cannot be all achieved, while an amount of sulfur compound (1) alone or a total weight of (1)+(2) of more than 20 parts by weight is not desirable since the scorch resistance of the unvulcanized rubber deteriorates.

[0092] As the reinforcing filler compounded into the rubber composition according to the present invention, those generally blended in for rubber use in the past, such as carbon black, silica, clay, talc, or surface-treated carbon black may be mentioned. The amount of the reinforcing filler compounded is preferably 40 to 150-parts by weight-based upon 100 parts by weight of the vulcanizable rubber. In particular, among these, a rubber composition containing 10 to 40 parts by weight of silica and containing a silane coupling agent conventionally compounded together with the rubber composition to an amount of 1 to 20% by weight of the amount of silica blended is preferable in that the high temperature tan δ is reduced compared with a composition not using the same.

[0093] As the cross-linking structure in the second aspect of the present invention, specifically the disulfide bridges are made not more than 2.5 times the monosulfide bridges, more preferably the ratio of the monosulfide bridges causing deterioration of the failure characteristics is made not more than 30% of the whole and the ratio of the polysulfide bridges is made not less than 40%. Further, in the present invention, since a specific organic polysulfide polymer having a tetrasulfide structure is used, even in the case of a polysulfide bridge of three or more sulfur atoms, while it may have as much as eight ordinary sulfur atoms, the number of sulfur bonds is kept down to not more than 4, and therefore, the heat aging characteristics are improved. Further, the sulfur compound of the present invention can greatly shorten the vulcanization time compared with known polysulfide polymer. As the means for obtaining this cross-linking structure, combination with a vulcanization accelerator is best. It is preferable to compound at least one vulcanization accelerator selected from a sulfenamide base, thiazole base, thiuram base, and dithio acid salt base accelerator to give a ratio by weight with the polysulfide polymer of preferably 0.3 to 5, and more preferably 0.3 to 3 and further to compound, into the above combination of the vulcanization accelerator at least vulcanization accelerator selected from a guanidine base, aldehyde-ammonia base, aldehyde-amine base, and thiourea base accelerator to 0.1 to 1 part by weight.

[0094] As explained above, the vulcanized rubber composition according to the present invention is a rubber composition containing a vulcanizable rubber, a reinforcing filler, and a sulfur compound (1) of the formula (I) which is vulcanized, where the ratio (VM/VD) of the value VM found from the degree of change before and after toluene swelling of the vulcanized rubber composition treated in a lithium aluminum hydride saturated tetrahydrofuran/toluene (ratio by volume 1/1) mixed solution using the formula (A) and the value VD found from the degree of change before and after toluene swelling of the vulcanized rubber composition treated in a propane-2-thiol (0.4 mol/l)/piperidine (0.4 mol/l) added tetrahydrofuran/toluene (ratio by volume 1/1) mixed solution using the formula (D) is not less than 0.4, more preferably where the ratio (VM/VT) of VT found from the degree of change before and after toluene swelling of the untreated vulcanized rubber composition using formula (C) and VM is not more than 0.3, more preferably not more than 0.15.

[0095] The formulas (A), (D), and (C) are generally known as Flory-Rehner formulas for finding the cross-linking density of vulcanized rubber from the swelling degree (ratio of change of volume of a vulcanized rubber before and after immersion in a good solvent). Details of these are given in P. J. Flory, J. Rehner, Journal of Chemical Physics, 11, 521 (1943). As a good solvent for causing swelling of rubber, benzene, toluene, n-hexane, acetone, ethanol, etc. may be mentioned, but in particular toluene is generally used. The μ in the formula, that is, the rubber-toluene interaction coefficient, is determined by the type of the rubber. In the case of natural rubber and isoprene rubber, μ=0.41 (room temperature), in the case of a styrene-butadiene copolymer rubber, μ=0.36 (room temperature, and in the case of a butadiene rubber, μ=0.32 is appropriate, as mentioned above.

[0096] The means for analyzing the sulfur cross-linking structure of vulcanized rubber and the reagents for cleaving the sulfur bridges are described above.

[0097] The present inventors performed the cleaving reaction in accordance with Nakauchi, Naito, Utsunomiya, Masuda, and Inoue, Journal of the Japan Rubber Association, vol. 60, No. 5, 267 (1987).

[0098] Here, the VT obtained from the toluene swell of vulcanized rubber not treated for a cleaving reaction using formula (C) is the measure of the overall bridge density. The VM obtained from the toluene swell of the vulcanized rubber treated by lithium aluminum hydride using formula (A) is the measure of the monosulfide bridge density. Therefore, the VD obtained using formula (D) is the monosulfide +disulfide bridge density minus the monosulfide bridge density, obtained from the toluene swell of vulcanized rubber treated by propane-2-thiol/piperidine, and is the measure of the disulfide bridge density.

[0099] The present inventors calculated the VM/VD and the VM/VT from the values VM, VD, and VT obtained from these formulas.

[0100] A VM/VD of less than 0.4 is not preferable since the disulfide bridge component for achieving both good failure characteristics and fatigue failure characteristics and heat aging characteristics is reduced, the balance is lost, and deterioration of the failure characteristics and the fatigue failure characteristics is induced. Further, a VM/VT of more than 0.3 is not preferable since the increase in the monosulfide bridge component causes deterioration of the failure characteristics and the fatigue failure characteristics.

[0101] As the sulfur compound of the formula (I) used in the present invention, mention may be made of polysulfide polymer having a Mooney viscosity of the material (measured in accordance with JIS K6300 using an L-shaped rotor with preheating at 100° C. for 1 minute and turning the rotor for 4 minutes) of not more than 100, preferably not more than 85, and having a number average molecular weight of 200 to 15000, preferably 1000 to 12000, a polysulfide polymer has the formula (III) to which sulfur is added in the backbone and having y of 3 to 5 on average and z of 3 to 5 on average:

R³S_(z)R²(S_(y)R²)_(m)S_(z)R³  (III)

[0102] wherein R² is a C₂ to C₁₀ oxyalkylene group and/or a C₂ to C₁₀ and O₂ to O₁₀, polyoxyalkylene group, R³ is at least one type of functional group selected from a C₁ to C₃₀ hydrocarbon group, preferably a C₃ to C₂₀ hydrocarbon group (for example, an allyl group, benzyl group, etc.), y is a number of 1 to 6, preferably 2 to 3, on average, z is a number of 1 to 6, preferably 2 to 3, on average, and m is an integer of 1 to 50, preferably 5 to 40, which polysulfide polymer has an R² of formula (III) shown by the following formula (IV):

—C₂H₄OC_(m′)H_(2m′)OC₂H₄—  (IV)

[0103] wherein m′ is an integer of 1 or 2, etc.

[0104] In a preferable embodiment of the vulcanized rubber composition according to the present invention, at least one vulcanization accelerator (3) selected from thiazole base, sulfenamide base, thiuram base, and dithio acid salt base accelerators is compounded in an amount of 0.5 to 5 parts by weight, preferably 0.3 to 2.5, of the polysulfide polymer so as to give a ratio by weight of the vulcanization accelerator and the polysulfide polymer of 0.3 to 4, preferably 0.3 to 2.

[0105] As the vulcanization accelerator, it is possible to further compound at least one vulcanization accelerator selected from a guanidine base; aldehyde-ammonia base, aldehyde-amine base, and thiourea base accelerator to 0.05 to 1 part by weight, preferably 0.05 to 0.7 part by weight, based upon 100 parts by weight of the starting rubber.

[0106] As the vulcanization agent of the present invention, the above sulfur compound (1) alone or the above sulfur compound (1) and sulfur (2) (or another sulfur donor) can be used. As this sulfur (2), it is possible to use any sulfur being used for vulcanization of ordinary rubber. As the form of the same, sublimated sulfur, precipitated sulfur, flower of sulfur, colloidal sulfur, etc. may be mentioned.

[0107] In the vulcanized rubber composition according to the present invention, the sulfur compound (1) of the formula (I) is used in an amount of 20 parts by weight or less, preferably 1-10 parts by weight, more preferably 1-4 parts by weight, based upon 100 parts of the rubber, or the sulfur compound (1) and the sulfur (2) are blended in at a ratio of (1)/(2) by weight of not less than 0.5, preferably 0.6 to 5.0, in a total weight of (1) +(2) of not more than 20 parts by weight, preferably 1 to 10 parts by weight, based upon 100 parts by weight of vulcanizable rubber. A ratio (1)/(2) of less than 0.5 is not desirable since the desired cross-linking structure is not obtained and good failure characteristics and fatigue characteristics and heat aging characteristics cannot be all achieved, while a weight of (1) or a total weight of (1)+(2) of more than 20 parts by weight is not desirable since the scorch resistance of the unvulcanized rubber deteriorates.

[0108] As the reinforcing filler blended into the rubber composition according to the present invention, ones generally blended in for rubber use in the past, such as carbon black, silica, clay, talc, or surface-treated carbon black may be mentioned. The amount of the reinforcing filler blended in is preferably 40 to 150 parts by weight, based upon 100 parts by weight of the vulcanizable rubber. In particular, among these, a rubber composition containing 10 to 40 parts by weight of silica and containing a silane coupling agent conventionally blended in together with the rubber composition to an amount of 1 to 20% by weight of the amount of silica blended is preferable in that the high temperature tan δ is reduced compared with a compositions not using the same.

[0109] Specific examples of the vulcanization accelerators which can be used in the second aspect of the present invention are as mentioned above.

[0110] As the vulcanizable rubber used in the present invention, for example any vulcanizable rubber generally used in for tire or other rubber applications in the past, specifically natural rubber (NR), butadiene rubber (BR), isoprene rubber (IR), chloroprene rubber (CR), butyl rubber (IIR), various styrene-butadiene rubbers (SBR), and other diene base rubbers or mixtures of the same may be mentioned.

[0111] As the vulcanization agent of the present invention, in addition to the above sulfur compound, sulfur and/or another sulfur donor may be used. As this sulfur, it is possible to use any sulfur being used for vulcanization of ordinary rubber. As the form of the same, sublimated sulfur, precipitated sulfur, flower of sulfur, colloidal sulfur, etc. may be mentioned.

[0112] The compounding ratio of the rubber composition according to the present invention is not particularly limited, but preferably the sulfur compound having the formula (I) is blended in an amount of 0.3 to 3.5 parts by weight, in terms of effective sulfur, based upon, 100 parts by weight of the vulcanizable rubber. If the amount of the sulfur is too small, vulcanization does not occur and sufficient physical properties are not obtained, while conversely if too large, scorching and other poor processability are caused.

[0113] As the reinforcing filler used in the rubber composition according to the present invention, those generally compounded for rubber use in the past, such as carbon black, silica, clay, talc, or surface-treated carbon black may be mentioned. The amount of the reinforcing filler blended in is preferably 40 to 120 parts by weight with respect to 100 parts by weight of the vulcanizable rubber.

[0114] The rubber composition according to the present invention may contain, in addition to the above essential ingredients, other ingredients generally used for blending in rubber such as other fillers, promoters such as zinc oxide and magnesium oxide, waxes, antioxidants, anti ozone crack agents, masticating accelerants, viscous resins, processing oils, and vulcanization retarders. The amounts compounded are within the general ranges unless impairing the object of the present invention.

[0115] As the vulcanization agent of the second aspect of the present invention, in addition to the above sulfur compound (1), sulfur (2) (or another sulfur donor) can also be used. As this sulfur (2), it is possible to use any sulfur being used for vulcanization of ordinary rubber. As the form of the same, sublimated sulfur, precipitated sulfur, flowers of sulfur, colloidal sulfur, etc. may be mentioned.

[0116] In the vulcanized rubber composition according to the second aspect of the present invention, at least one vulcanization accelerator (3) selected from a thiazole base, sulfenamide base, thiuram base, and dithio acid salt base accelerator is used in an amount of 0.3 to 5 parts by weight, preferably 0.3 to 2.5 parts by weight, based upon 100 parts by weight of the vulcanizable rubber. By compounding such a vulcanization accelerator, it becomes possible to obtain a desired cross-linking structure and possible to balance the failure characteristics, fatigue characteristics, heat aging characteristics, and heat buildup property.

[0117] As the vulcanization accelerator, it is possible to further compound at least one vulcanization accelerator selected from a guanidine base, aldehyde-ammonia base, aldehyde-amine base, and thiourea base accelerator to 0.05 to 1 part by weight, preferably 0.05 to 0.7 part by weight, based upon 100 parts by weight of vulcanizable rubber.

[0118] Specific examples of the vulcanization accelerators which can be used in the present invention are exemplified above:

[0119] As the vulcanizable rubber used in the second aspect of the present invention, for example any vulcanizable rubber generally compounded for tire use or other rubber applications in the past, specifically natural rubber (NR), butadiene rubber (BR), isoprene rubber (IR), chloroprene rubber (CR), butyl rubber (IIR), various styrene-butadiene rubbers (SBR), and other diene base rubbers or mixtures of the same may be mentioned. Note that by making 10 to 60 parts by weight in the 100 parts by weight of vulcanizable rubber a polybutadiene rubber, the high temperature side tan δ is reduced and the heat buildup property is improved.

[0120] It is preferable that the vulcanized rubber composition according to the present invention contain therein an anti-scorch agent such as for example N-(cyclohexylthio)phthalimide in an amount of 0.05 to 1 part by weight based upon 100 parts by weight of the vulcanizable rubber so as to give a superior scorch resistance and increase the ratio of disulfide cross-linking.

[0121] The rubber composition according to the present invention may contain, in addition to the above essential ingredients, other ingredients generally used in rubber use, as mentioned above.

[0122] As explained above, the rubber composition according to the third aspect of the present invention contains a vulcanizable rubber, a reinforcing filler, a sulfur compound (1) of the formula (I), and sulfur (2).

[0123] The sulfur compound (1) of the formula (I) used in the third aspect of the present invention are those mentioned above.

[0124] As the vulcanization agent of the third aspect of the present invention, in addition to the above sulfur compound (1), sulfur (2) (or another sulfur donor) is used. As this sulfur (2), it is possible to use any sulfur being used for vulcanization of ordinary rubber. As the form of the same, sublimated sulfur, precipitated sulfur, flowers of sulfur, colloidal sulfur, etc. may be mentioned.

[0125] In the vulcanized rubber composition according to the third aspect of the present invention, the sulfur compound (1) of the formula (I) and the sulfur (2) are blended in at a ratio of (1)/(2) by weight of less than 0.5, preferably 0.2 to 0.5, in a total weight of (1)+(2) of not more than 20 parts by weight, preferably 2 to 10 parts by weight, with respect to 100 parts by weight of vulcanizable rubber. A ratio (1)/(2) of 0.5 or more is not desirable since the other mechanical properties and heat buildup property deteriorate, while a total weight of (1)+(2) of more than 20 parts by weight is not desirable since the scorch property of the unvulcanized rubber remarkably deteriorates.

[0126] In a preferable embodiment of the vulcanized rubber composition according to the third aspect of the present invention, the polysulfide polymer is compounded in an amount of 0.5 to 5 parts by weight, preferably 0.5 to 3 parts by weight, and at least one type of vulcanization accelerator selected from a thiazole base, sulfenamide base, thiuram base, and dithio acid salt base accelerator is compounded in to 0.3 to 3 parts by weight.

[0127] As the vulcanization accelerator, it is possible to further compound at least one vulcanization accelerator selected from a guanidine base, aldehyde-ammonia base, aldehyde-amine base, and thiourea base accelerator to 0.05 to 1 part by weight, preferably 0.05 to 0.7 part by weight, based upon 100 parts by weight of the vulcanizable rubber.

[0128] Specific examples of the vulcanization accelerators which can be used in the present invention are those mentioned above As the vulcanizable rubber used in the third aspect of the present invention, for example, any vulcanizable rubber generally used in tire use or other-rubber applications in the past, specifically natural rubber (NR), butadiene rubber (BR), isoprene rubber (IR), chloroprene rubber (CR), butyl rubber (IIR), various styrene-butadiene rubbers (SBR), and other diene base rubbers or mixtures of the same may be mentioned.

[0129] As the reinforcing filler compounded in the rubber composition according to the present invention, ones generally used in for rubber use in the past, such as carbon black, silica, clay, talc, or surface-treated carbon black may be mentioned. The amount of the reinforcing filler is preferably 40 to 120 parts by weight based upon 100 parts by weight of the vulcanizable rubber.

[0130] The rubber composition according to the present invention may have added to it, in addition to the above essential ingredients, other ingredients generally used in rubber as mentioned above.

[0131] As the diene base rubber to be compounded into the rubber composition of the fourth aspect of the present invention, for example any diene rubber generally used in tire use or other rubber applications in the past, specifically, natural rubber (NR), butadiene rubber (BR), isoprene rubber (IR), chloroprene rubber (CR), butyl rubber (IIR), various types of styrene-butadiene rubbers (SBR), and other diene-base rubbers or mixtures thereof may be mentioned.

[0132] As the reinforcing filler used in the rubber composition according to the fourth aspect of the present invention, ones generally-blended in for rubber use in the past, such as carbon black and silica, may be mentioned. The amount of the reinforcing filler is 40 to 85 parts by weight, preferably 45 to 75 parts by weight, based upon 100 parts by weight of diene rubber. Note that when compounding silica, it is preferable to compound 0.1 to 15% by weight of a general use silane coupling agent (for example, vinyl trichlorosilane, vinyl trimethoxysilane, vinyl triethoxysilane, vinyl tris(β-methoxyethoxy)silane, β-(3,4-epoxycyclohexyl)ethyl trimethoxysilane, γ-glycidoxypropyl trimethoxysilane, γ-glycidoxypropylmethyl diethoxysilane, γ-glycidoxypropyl triethoxysilane, γ-methacryloxypropylmethyl dimethoxysilane, γ-methacryloxypropyl trimethoxysilane, γ-methacryloxypropylmethyl diethoxysilane, γ-methacryloxypropyl triethoxysilane, N-β(aminoethyl)γ-aminopropylmethyl dimethoxysilane, N-β(aminoethyl)γ-aminopropyl trimethoxysilane, N-β(aminoethyl)γ-aminopropyl triethoxysilane, γ-aminopropyl trimethoxysilane, γ-aminopropyl triethoxysilane, N-phenyl-γ-aminopropyl trimethoxysilane, γ-chloropropyl trimethoxysilane, γ-mercaptopropyltrimethoxysilane, bis-(3-[triethoxysilyl]-propyl)-tetrasulfane, etc.) with respect to the weight of the silica as is the general practice in the past.

[0133] The rubber composition according to the fourth aspect of the present invention further contains therein a rosin base resin and/or cyclopentadiene base resin. The amount of these resins compounded is 1 to 10 parts by weight, preferably 3 to 8 parts by weight, based upon 100 parts by weight of the diene rubber. When an amount of those resin is too small, it is not desirable since it becomes difficult to secure a high hardness and a high elongation at break and the cut resistance is liable to fall on poor roads and under heavy duty conditions, while the amount is too large, it is not desirable since the heat buildup rises and a fall in the durability is liable to be induced.

[0134] Examples of the rosin base resins usable in the fourth aspect of the present invention, gum rosins, wood rosins, tall oil rosins, etc. mainly comprised of abietic acid, neoabietic acid, pimaric acid, isopimaric acid, dehydroabietic acid. It is also possible to use disproportionated rosins obtained by disproportionation of these rosins and hydrogenated rosins obtained by hydrogenation.

[0135] Further, in the present invention, it is possible to partially maleate and/or fumarate the rosins. By maleation and/or fumaration, the effect of improvement of the heat buildup property becomes greater. For the maleation of a rosin, anhydrous maleic acid is used, while for fumaration of a rosin, fumaric acid is used. The addition reaction of the anhydrous maleic acid and/or fumaric acid to the rosin may be performed by a known method. For example, it may be done by heating and melting the stock rosin, then adding anhydrous maleic acid and/or fumaric acid to this. Further, the reaction may be performed either under pressure or at ordinary pressure.

[0136] The cyclopentadiene base resin usable in the present invention means cyclopentadiene or dicyclopentadiene and copolymers thereof with copolymerizable olefin base hydrocarbons or polymers of cyclopentadiene and/or dicyclopentadiene, but in the case of a copolymer it is preferably one containing at least 30% by weight of cyclopentadiene, dicyclopentadiene, or a mixture of cyclopentadiene and dicyclopentadiene, more preferably at least 50% by weight.

[0137] The olefin base hydrocarbon copolymerizable with cyclopentadiene or dicyclopentadiene referred to here means an olefin base hydrocarbon such as 1-butene, 2-butene, isobutylene, 1-pentene, 2-pentene, 2-methyl-1 butene, 3-methyl-1 butene, and 2-methyl-2 butene, a diolefin base hydrocarbon such as butadiene, isoprene, and 3-methylbutadiene 1.2, and a vinyl aromatic hydrocarbon such as styrene, α-methylstyrene, and vinyl toluene and can be copolymerized by a Friedel-Crafts reaction with cyclopentadiene or dicyclopentadiene in the presence of a suitable catalyst.

[0138] Further, the softening point of these cyclopentadiene base resins (ring and ball method, JIS K-5902) is preferably 50 to 200° C., more preferably 80 to 150° C. The bromine value (ASTM D-1158-57T) is preferably 40 to 150, more preferably 50 to 150. This is preferable in respect to the molecular weight for securing the cut resistance and the reactivity of the double bonds.

[0139] According to the first embodiment of the fourth aspect of the present invention, the sulfur compound (I) is used as the sulfur compound. As the sulfur compound (I) used in the present invention, a polysulfide polymer having a molecular weight of 200 to 15000, preferably 1000 to 12000, and a polysulfide polymer of the formula (III):

R³S_(z)R²(S_(y)R²)_(m)S_(z)R³  (III)

[0140] wherein R² is a C₂ to C₁₀ oxyalkylene group and/or C₂ to C₁₀ and O₂ to O₁₀ polyoxyalkylene group, R³ is at least one functional group selected from C₁ to C₃₀, preferably C₃ to C₂₀ hydrocarbon groups (for example, allyl group, benzyl group, etc.), y is a number from 2.0 to 5.0, and m is an integer of 1 to 50, preferably 5 to 40, to which sulfur is added in the backbone and in which y is an average of over 3 to up to 5 and z is 1 to 5, preferably 1 to 3, which polysulfide polymer has an R² of formula (III) of the following formula (IV):

—C₂H₄OC_(m′)H_(2m′)OC₂H₂—  (IV)

[0141] wherein m′ is an integer of 1 to 2 may be mentioned.

[0142] According to the second embodiment of the fourth aspect of the present invention, the sulfur compound (II). is used as the sulfur compound. This sulfur compound may be synthesized by a reaction of an alkali metal salt of 2-mercaptobenzothiazole with sulfur chloride, sulfur dichloride, or mixtures thereof. For example, 2 moles of 2-mercaptobenzothiazole sodium salt and 1 mole of sulfur chloride are allowed to react at room temperature to a reflux temperature for 4 hours to 20 hours using alcohol as a reaction solvent. Next, after the reaction is finished, an excess amount of water is added and the resultant mixture filtered. The residue is further washed with water and the unreacted 2-mercaptobenzothiazole sodium salt and sulfur chloride are removed. The reaction product obtained is dried, then recrystallized by, for example, methanol so as to obtain a sulfur compound (II) of a melting point of 116 to 118° C.

[0143] As the sulfur compound used in the present invention, it is possible to jointly use, in addition to the sulfur compound (I) and/or (II), if necessary or desired, sulfur and/or another sulfur donor. As such sulfur, it is possible to use any sulfur being used for ordinary rubber vulcanization. The types include sublimated sulfur, precipitated sulfur, flowers of sulfur, colloidal sulfur, etc.

[0144] As the sulfur donor capable of being jointly used with the sulfur compound of formula (I) and/or (II) in the present invention, it is possible to mention for example the polysulfide rubbers described in the Society of Rubber Industry Japan ed., Rubber industry Handbook <New Edition>, Nov. 15, 1973, p. 169. Specifically, poly(ethylenetetrasulfide), poly(propylenetetrasulfide), and poly(tetraethylenesulfide) may be mentioned.

[0145] Further, it is possible to use the sulfur base sulfur compounds described in CMC ed. (Jan. 6, 1988), Latest Technology in Polymer Addition Agents, pp. 298 to 299. Specifically, N,N′-dithiodi(polymethylenimide) and N,N′-bis(2-benzothiazolylthio)piperadine may be mentioned.

[0146] Further, the vulcanization accelerators called the SSO and SSS type described in Japanese Unexamined Patent Publication (Kokai) No. 47-9488, Japanese Unexamined Patent Publication (Kokai) No. 47-5391, and Japanese Examined Patent Publication (Kokoku) No. 57-15611 (for example, 2,4-di(O,O′-diisopropylphosphotrithioyl)-6-morpholino-1,3,5-triazine and 2-(O,O′-diisopropylphosphotrithioyl)-4,6-di(N,N-diethylamino)-1,3,5-triazine) may also be suitably mentioned as sulfur donors for the present invention.

[0147] The ratio of use of the sulfur compound (I) and/or (II) and the other sulfur or sulfur donor in the present invention is not particularly limited, but preferably at least 15% by weight, more preferably at least 30% by weight, in terms of the effective sulfur, of the sulfur compound (I) and/or (II) is used based upon the total amount of effective sulfur.

[0148] The ratio of formulation in the rubber composition according to the present invention is not particularly limited, but preferably 0.5 to 3 parts by weight, preferably 1.0 to 2.5 parts by weight, in terms of effective sulfur, is blended into 100 parts by weight of diene rubber. Of the amount of sulfur blended is too small, it is not desirable since vulcanization does not occur and sufficient physical properties are liable not to be obtained, while too large an amount is not desirable since the heat aging characteristics are liable to fall.

[0149] The sulfur compound of the present invention enables sufficient vulcanization even without use of a vulcanization accelerator, but it is also possible to use a thiazole base, sulfenamide base, thiuram base, dithiocarbamate base, guanidine base, thiourea base, dithiophosphate base, xanthate base, or other accelerator. In particular, a guanidine base vulcanization agent (for example, diphenyl guanidine, diorthotolyl guanidine, and orthotblyl (bi)guamide) is preferably jointly used in an amount of 0.01 to 1.5 parts by weight based upon 100 parts by weight of the diene rubber, whereby an improvement in the heat aging characteristics due to the lesser fall in the elongation at break (EB) after heat aging and an improvement in the appearance after use along with the same are observed.

[0150] The rubber composition according to the fourth aspect of the present invention may further contain therein, as other ingredients, additives generally used for rubber, as mentioned above.

[0151] The rubber composition for heavy duty tire tread use according to the present invention may be produced as a heavy duty tire tread by processing according to a conventional general method of production. It may be used for production of a tire without requiring any new steps.

EXAMPLES

[0152] The present invention will now be further illustrated by, but is by no means limited to, the following Examples, wherein all parts and percentages are expressed on a weight basis unless otherwise noted.

[0153] Examples 1 to 11 and Comparative Examples 1 to 14

[0154] Preparation of Samples

[0155] The ingredients of the master batch of the following formulation (parts by weight) were mixed in a closed type mixer for 3 to 5 minutes. The contents thereof were discharged when reaching about 165° C. Master batch IR (Nippon Zeon, Nipol IR 2200) 100.0 N339 carbon black (Tokai Carbon, 50.0 Seast KH) Zinc oxide (Zinc White No. 3) 3.0 Industrial use stearic acid 1.0 Antioxidant 6C*¹ 1.0 Total 155.0

[0156] diamine

[0157] The vulcanization agents and vulcanization accelerators (parts by weight) shown in Tables I and II were mixed into the master batch obtained by an open roll to obtain the rubber compositions.

[0158] Next, the rubber compositions obtained were press vulcanized in 15×15×0.2 cm molds at 160° C. for 20 minutes to prepare the desired test pieces which were then evaluated as to vulcanized physical properties before and after aging (100° C.×96 hours). The resultant compositions are shown in Tables I and II.

[0159] Further, the VM, VD, and VT were measured as follows:

[0160] 15×15×0.2 cm vulcanized test pieces were cut out and 0.2×0.2×0.2 cm rubber samples were prepared. These rubber samples were Soxhlet extracted using acetone, dried, precisely measured for volume, immersed for cleaving treatment in a lithium aluminum hydride saturated tetrahydrofuran/toluene mixed solution and propane-2-thiol/piperidine added tetrahydrofuran/toluene mixed solution, then rinsed. The Soxhlet extracted untreated rubber samples, the lithium aluminum hydride treated rubber samples, and the propane-2-thiol/piperidine treated rubber samples were immersed in toluene for a long period of time, then precisely measured for swelled volume and the degrees of change before and after toluene swelling were calculated. The volume percentage of the reinforcing filler was calculated from the formulation Table.

[0161] The molar volume of the toluene was 106.3. The rubber and toluene interaction constant μ, since isoprene rubber is used, was 0.41.

[0162] The test methods of the vulcanized physical properties were as follows:

[0163] Dispersion at time of roll mixing: The degree of mixing of the master batch and organic sulfur compound was judged visually.

[0164] Good: State where the master batch and organic sulfur compound are compatible and sufficiently mixed together

[0165] Poor: State where the organic sulfur compound is scattered in granular form and poor dispersion is caused

[0166] Vulcanization time T₉₅ (150° C.) (minutes): Time (minutes) until reaching 95% vulcanization degree at 150° C. based on JIS K6301

[0167] Strain at 100% elongation (MPa): Measured in accordance with JIS K6301 (dumbbell type No. 3)

[0168] Elongation strength at break (MPa): Measured in accordance with JIS K6301 (dumbbell type No. 3)

[0169] Elongation at break (%): Measured in accordance with JIS K6301 (dumbbell type No. 3)

[0170] Crack growth length (mm): Measured according to JIS K6301. The crack length after 100,000 flexings was measured in mm units. TABLE I-1 Comp. Comp. Comp. Comp. Comp. Comp. Comp. Comp. Comp. Ex. I-1 Ex. I-2 Ex. I-3 Ex. I-4 Ex. I-5 Ex. I-6 Ex. I-7 Ex. I-8 Ex. I-9 IR base master batch 155 155 155 155 155 155 155 155 155 Powdered sulfur 1.50 1.50 2.00 — 1.50 1.50 — — — Vulcanization accelerator 1 (CBS) 1.20 — — — — — — — — Vulcanization accelerator 2 (TBBS) — 1.00 — — 1.00 1.00 1.00 5.00 1.00 Vulcanization accelerator 3 (MBTS) — — 1.40 — — — — — — Vulcanization accelerator 4 (TETD) — — — 3.50 — — — — — Vulcanization accelerator 5 (DPG) — — — — 0.20 — — — 1.10 Vulcanization accelerator 6 (DOTU) — — — — — 0.20 — — — Polysulfide 1 — — — — — — 5.00 1.40 3.00 Ratio of amount of polysulfide — — — — — — 5.00 0.28 3.00 added/amount of accelerator added VM (×10⁻⁵ mol/cc) 2.5 2.2 2.3 13.1 2.6 2.8 1.4 5.1 2.7 VD (×10⁻⁵ mol/cc) 4.5 4.3 4.1 1.1 4.9 5.1 2.7 4.2 6.1 VT (×10⁻⁵ mol/cc) 15.1 15.2 15.3 14.8 15.4 15.9 15.3 14.2 15.4 VM/VT 0.17 0.14 0.15 0.89 0.17 0.18 0.09 0.36 0.18 VM/VD 0.56 0.51 0.56 11.91 0.53 0.55 0.52 1.21 0.44 T₉₅ at 150° C. (min) 9.2 10.1 14.1 23.5 8.5 7.9 25 7.5 23 (Not yet aged) Stress at 100% elongation (MPa) 2.9 2.9 2.9 2.8 2.9 3.0 2.9 2.7 2.9 Elongation strength at break (MPa) 31.5 32.1 33.8 27.2 30.9 30.5 33.7 21.1 25.8 Elongation at break (%) 502 486 452 498 462 455 511 398 431 Crack growth length (mm) 11 9 8 Break 13 14 8 Break 25 (Aged at 100° C. × 96 hr) Stress at 100% elongation (MPa) 4.2 4.2 3.8 3.5 4.1 4.1 4.1 3.1 3.5 Elongation strength at break (MPa) 14.2 16.7 20.3 23.4 18.5 19.8 19.5 18.4 18.8 Elongation at break (%) 246 277 294 398 300 296 322 326 323 Crack growth length (mm) 23 18 17 45 17 17 19 45 29 Ex. I-1 Ex. I-2 Ex. I-3 Ex. I-4 Ex. I-5 Ex. I-6 Ex. I-7 Ex. I-8 IR base master batch 155 155 155 155 155 155 155 155 Powdered sulfur — — — — — — 0.80 0.90 Vulcanization accelerator 1 (CBS) 1.20 — — — — — — — Vulcanization accelerator 2 (TBBS) — 1.00 — 0.75 1.00 1.00 1.00 1.00 Vulcanization accelerator 3 (MBTS) — — 1.40 — — — — — Vulcanization accelerator 4 (TETD) — — — 1.00 — — — — Vulcanization accelerator 5 (DPG) — — — — 0.20 — 0.20 0.40 Vulcanization accelerator 6 (DOTU) — — — — — 0.20 — — Polysulfide 1 3.20 3.00 3.50 2.00 3.00 3.00 1.50 1.50 Ratio of amount of polysulfide added/amount 2.67 3.00 2.50 1.14 3.00 3.00 1.50 1.50 of accelerator added VM (×10⁻⁵ mol/cc) 1.4 1.5 1.9 2.2 1.8 2 2.8 3.1 VD (×10⁻⁵ mol/cc) 4.6 5 6.3 6.8 5.3 5.6 7.1 7.8 VT (×10⁻⁵ mol/cc) 15.1 15.4 14.6 15.2 15.7 15.8 16.1 16.3 VM/VT 0.09 0.10 0.13 0.14 0.11 0.13 0.17 0.19 VM/VD 0.30 0.30 0.30 0.32 0.34 0.36 0.37 0.40 T₉₅ at 150° C. (min) 14.6 27.1 35.2 30.4 24.2 22.1 14.1 12.5 (Not yet aged) Stress at 100% elongation (MPa) 2.9 2.9 2.8 2.9 3.0 3.0 3.1 3.1 Elongation strength at break (MPa) 34.2 33.5 30.1 29.7 32.5 31.7 32.1 32.3 Elongation at break (%) 535 532 509 513 540 528 548 541 Crack growth length (mm) 14 12 15 20 17 18 11 13 (Aged at 100° C. × 96 hr) Stress at 100% elongation (MPa) 3.7 3.8 3.6 3.8 3.9 3.9 4.1 4.0 Elongation strength at break (MPa) 28.7 28.1 25.3 24.9 27.3 26.6 26.3 26.5 Elongation at break (%) 449 447 428 431 470 459 455 449 Crack growth length (mm) 15 13 16 22 17 18 18 15

[0171] Table I-1 Footnotes

[0172] Note) Samples having relatively low molecular weights can be measured for molecular weight, but rubber-like high molecular weights samples cannot be determined, and therefore, the Mooney viscosity is used instead.

[0173] 1) Preparation of polysulfide 1 (4 sulfur atoms, molecular weight 10,000, end alkyl)

[0174] Polysulfide 1 (4 Sulfur Atoms, Allyl End)

[0175] An excess of allyl chloride was added to a polysulfide polymer (Toray Thiokol, LP-32) in the presence of an equivalent amount of triethylamine to cause a reaction. The amine hydrochloride was filtered out, then the excess allyl chloride was distilled off. 36.2 g of powdered sulfur and 0.5 g of triethylamine were added to 100 g of this polymer and a reaction caused at 90° C. for 1 hour to obtain a viscous polysulfide (average molecular weight of about 5500).

[0176] Polysulfide 2 (6 Sulfur Atoms, Allyl End)

[0177] An excess of allyl chloride was added to a polysulfide polymer (Toray Thiokol, LP-32) in the presence of an equivalent amount of triethylamine to cause a reaction. The amine hydrochloride was filtered out, then the excess allyl chloride was distilled off. 72.4 g of powdered sulfur and 0.5 g of triethylamine were added to 100 g of this polymer and a reaction caused at 90° C. for 1 hour to obtain a viscous polysulfide (average molecular weight of about 7000).

[0178] Polysulfide 3 (2 Sulfur Atoms, Allyl End)

[0179] An excess of allyl chloride was added to a polysulfide polymer (Toray Thiokol, LP-31) in the presence of an equivalent amount of triethylamine to cause a reaction. The amine hydrochloride was filtered out, then the excess allyl chloride was distilled off to obtain a viscous polysulfide (average molecular weight of about 8000).

[0180] Polysulfide 4 (4 Sulfur Atoms, Benzyl End)

[0181] An excess of benzyl chloride was added to a polysulfide polymer (Toray Thiokol, LP-31) in the presence of an equivalent amount of triethylamine to cause a reaction. The amine hydrochloride was filtered out, then the excess benzyl chloride was distilled off. 36.9 g of powdered sulfur and 0.5 g of triethylamine were added to 100 g of this polymer and a reaction caused at 90° C. for 1 hour to obtain a viscous polysulfide (average molecular weight of about 11200).

[0182] Polysulfide 5 (4 Sulfur Atoms, Hydroxy End)

[0183] Three times the molar amount of ethylene oxide was reacted with a polysulfide polymer (Toray Thiokol, LP-32) in the presence of an alkali catalyst to convert the end to a hydroxyl group. 34.5 g of powdered sulfur and 0.5 g of triethylamine were added to 100 g of this polymer and a reaction caused at 90° C. for 3 hours to obtain a viscous polysulfide (average molecular weight of about 5500).

[0184] Polysulfide Rubber 1 (4 Sulfur Atoms, End Alkyl, Mooney Viscosity of about 80)

[0185] 31.6 g of 1,2-dichloroethane, 2.69 g of benzyl chloride, 141 g of sodium tetrasulfide (41% solution), and 50 g of methanol were added and reacted at room temperature for 1 hour, then rinsed to obtain a rubbery polysulfide.

[0186] Polysulfide Rubber 2 (4 Sulfur Atoms, Mooney viscosity of about 120)

[0187] 31.6 g of 1,2-dichloroethane, 135.5 g of sodium tetrasulfide (41%), and 50 g of methanol were used to obtain this in the same way as the polysulfide rubber 1.

[0188] 2) Vulcanization Accelerator

[0189] Vulcanization accelerator 1 (CBS): N-cyclohexyl-2-benzothiazole sulfenamide

[0190] Vulcanization accelerator 2 (TBBS): N-t-butyl-2-benzothiazole sulfenamide

[0191] Vulcanization accelerator 3 (MBTS): dibenzothiazyl sulfide

[0192] Vulcanization accelerator 4 (TETD): tetraethylthiuram disulfide

[0193] Vulcanization accelerator 5 (DPG): diphenyl guanidine

[0194] Vulcanization accelerator 6 (DOTU): diorthotolylthiourea TABLE I-2 Comp. Ex. Comp. Ex. Comp. Ex. Comp. Ex. Ex. I-9 I-10 I-11 Ex. I-10 I-12 Ex. I-11 I-13 IR base master batch 155 155 155 155 155 155 155 Vulcanization accelerator 2 1.00 1.00 1.00 1.00 1.00 1.00 1.00 (TBBS) Polysulfide 1 3.00 — — — — — — Polysulfide 2 — 3.00 — — — — — Polysulfide 3 — — 3.00 — — — — Polysulfide 4 — — — 3.00 — — — Polysulfide 5 — — — — 3.00 — — Polysulfide rubber 1 — — — — — 3.00 — Polysulfide rubber 2 — — — — — — 3.00 Ratio of amount of polysulfide 3.00 3.00 3.00 3.00 3.00 3.00 3.00 added/amount of accelerator added VM (×10⁻⁵ mol/cc) 1.6 2.1 12.1 1.2 1.2 0.9 1.1 VD (×10⁻⁵ mol/cc) 5.3 4.7 1.5 3.1 2.1 2.9 2.6 VT (×10⁻⁵ mol/cc) 15.6 15.2 14.1 15.7 14.8 16.2 14.7 VM/VT 0.10 0.14 0.86 0.08 0.08 0.06 0.07 VM/VD 0.30 0.45 8.07 0.39 0.57 0.31 0.42 Dispersion at roll mixing Good Good Good Good Good Good Poor T₉₅ (150° C., min) 25.1 19.5 46 21.1 41 29.3 36.3 (Not yet aged) Stress at 100% elongation (MPa) 3.0 2.8 1.9 3.2 2.9 2.3 1.8 Elongation strength at break (MPa) 33.8 33.1 18.7 34.2 34.2 34.1 19.4 Elongation at break (%) 541 538 580 546 539 550 581 Crack growth length (mm) 12 10 Break 18 11 20 Break (Aged at 10° C. × 96 hr) Stress at 100% elongation (MPa) 3.9 4.1 2.2 4.5 4.4 2.9 2.2 Elongation strength at break (MPa) 28.4 21.5 15.9 27.4 20.5 26.1 17.1 Elongation at break (%) 454 328 464 437 340 399 432 Crack growth length (mm) 13 19 40 21 20 21 Break

Examples II-1 to II-22 and Comparative Examples II-1 to II-28

[0195] Preparation of Samples

[0196] The ingredients of the master batches of the following formulations (parts by weight) were mixed in a closed type mixer for 3 to 5 minutes. The contents were discharged when reaching about 165° C. IR base master batch (parts by weight) IR (Nippon Zeon, Nipol IR 2200) 100 N339 carbon black (Tokai Carbon, Seast KH) 50 Zinc oxide (Zinc White No. 3) 3 Industrial use stearic acid 1 Antioxidant 6C*¹ 1 Total 155

[0197] diamine SBR base master batch (A) (parts by weight) SBR (Nippon Zeon, Nipol SBR 1502) 100 N220 carbon black (Tokai Carbon, 62 Seast KH) Zinc white 3 Industrial use stearic acid 1 Modified rosin resin 6 Oil 5 Antioxidant 6C*¹ 1 Total 178

[0198] diamine NR/BR base master batches (parts by weight) MB1 MB2 MB3 IR (Nippon Zeon, Nipol IR 100 90 70 2200) BR (Nippon Zeon, Nipol BR. — 10 30 1220) N339 carbon black (Tokai 50 50 50 Carbon, Seast KH) Zinc oxide (Zinc White No. 3 3 3 3) Industrial use stearic acid 2 2 2 Antioxidant 6C*¹ 2 2 2 Total 157 157 157

[0199] The vulcanization agents and vulcanization accelerators (parts by weight) shown in Tables II-1 to II-5 were kneaded into the master batches obtained by an open roll to obtain the rubber compositions.

[0200] Next, the rubber compositions obtained were press vulcanized in 15×15 ×0.2 cm molds at 160° C. for 20 minutes to prepare the desired test pieces which were then evaluated as to vulcanized physical properties before and after aging (100° C.×96 hours). The resultant compositions are shown in Tables II-1 to II-5.

[0201] Further, the VM, VD, and VT were measured as follows: 15×15×0.2 cm vulcanized test pieces were cut out and 0.2×0.2×0.2 cm rubber samples were prepared.

[0202] These rubber samples were Soxhlet extracted using acetone, dried, precisely measured for volume, immersed for cleaving in a lithium aluminum hydride saturated 20 tetrahydrofuran/toluene mixed solution and propane-2-thiol/piperidine added tetrahydrofuran/toluene mixed solution, then rinsed. The Soxhlet extracted untreated rubber samples, the lithium aluminum hydride treated rubber samples, and the propane-2-thiol/piperidine treated rubber samples were immersed in toluene for a long period of time, then precisely measured for swelled volume and the degrees of change before and after toluene swelling were calculated. The volume percentage of the reinforcing filler was calculated from the formulation Table.

[0203] The molar volume of the toluene was 106.3. The rubber and toluene interaction constant μ used was 0.41 in the case of isoprene rubber, 0.36 in the case of SBR (styrene-butadiene copolymer rubber), 0.40 in the case of a mixture of isoprene rubber and butadiene rubber where the ratio of isoprene rubber/butadiene rubber is 9/1, and 0.38 in the same case where the ratio of isoprene rubber/butadiene rubber is 7/3.

[0204] The test methods of the vulcanized physical properties were as follows:

[0205] Dispersion at time of roll mixing: The degree of mixing of the master batch and organic sulfur compound was judged visually.

[0206] Good: State where the master batch and organic sulfur compound are compatible and sufficiently mixed together

[0207] Poor: State where the organic sulfur compound is scattered in granular form and poor dispersion is caused

[0208] Vulcanization time T₉₅ (150° C.) (minutes): Time (minutes) until reaching 95% vulcanization degree at 150° C. based on JIS K6301

[0209] tan δ (60° C.): A Toyo Seiki Seisakusho viscoelasticity spectrometer (Rherosolid) was used for measurement at an amplitude of ±2% at 60° C., a frequency of 20 Hz, and an initial strain of 10%. Note that the larger the value of the tan δ (60° C.), the worse the heat buildup.

[0210] Strain at 100% elongation (MPa): Measured in accordance with JIS K6301 (dumbbell type No. 3)

[0211] Elongation strength at break (MPa): Measured in accordance with JIS K6301 (dumbbell type No. 3)

[0212] Elongation at break (%): Measured in accordance with JIS K6301 (dumbbell type No. 3)

[0213] Crack growth length (mm): Measured according to JIS K6301. The crack length after 100,000 flexings was measured in mm units. TABLE II-1 Comp. Comp. Comp. Comp. Comp. Comp. Comp. Comp. Comp. Ex. II-1 Ex. II-2 Ex. II-3 Ex. II-4 Ex. II-5 Ex. II-6 Ex. II-7 Ex. II-8 Ex. II-9 IR base master batch 155 155 155 155 155 155 155 155 155 Powdered sulfur 1.5 1.5 2.0 — 1.5 1.5 — — — Vulcanization accelerator 1 (CBS) 1.2 — — — — — — — 1.2 Vulcanization accelerator 2 (TBBS) — 1.0 — — 1.0 1.0 1.0 5.0 — Vulcanization accelerator 3 (MBTS) — — 1.4 — — — — — — Vulcanization accelerator 4 (TET) — — — 3.5 — — — — — Vulcanization accelerator 5 (DPG) — — — — 0.2 — — — — Vulcanization accelerator 6 (DOTU) — — — — — 0.2 — — — Polysulfide 1 — — — — — — 5.0 1.4 3.2 Polysulfide 2 — — — — — — — — — Polysulfide 3 — — — — — — — — — Polysulfide 4 — — — — — — — — — Polysulfide 5 — — — — — — — — — Ratio of amount of polysulfide — — — — — — — — — added/amount of sulfur added Ratio by weight of (polysulfide + 1.25 1.5 1.43 0.0 1.5 1.5 5.0 0.28 2.67 sulfur)/accelerator VM (×10⁻⁵ mol/cc) 2.5 2.2 2.3 13.1 2.6 2.8 1.4 5.1 1.4 VD (×10⁻⁵ mol/cc) 4.5 4.3 4.1 1.1 4.9 5.1 2.7 4.2 4.6 VM + D (×10⁻⁵ mol/cc) 7.0 6.5 6.4 14.2 7.5 7.9 4.1 9.3 6 VT (×10⁻⁵ mol/cc) 15.1 15.2 15.3 14.8 15.4 15.9 15.3 14.2 15.1 VM/VT 0.17 0.14 0.15 0.89 0.17 0.18 0.09 0.36 0.09 VM/VD 0.56 0.51 0.56 11.91 0.53 0.55 0.52 1.23. 0.30 (VT − VN + D)/VT 0.54 0.57 0.58 0.04 0.51 0.50 0.73 0.35 0.60 Vulcanization time T₉₅ (150° C.) 9.2 10.1 14.1 23.5 8.5 7.9 25.0 7.5 14.6 (min) tanδ (60° C.) 0.124 0.120 0.136 0.143 0.122 0.125 0.138 0.146 0.142 (Not yet aged) Stress at 100% elongation (MPa) 2.9 2.9 2.9 2.8 2.9 3.0 2.9 2.7 2.9 Elongation strength at break (MPa) 31.5 32.1 33.8 27.2 30.9 30.5 33.7 21.1 34.2 Elongation at break (%) 502 486 452 498 462 455 511 398 535 Crack growth length (mm) 11 9 8 Break 13 14 8 Break 14 (Aged at 100° C. × 96 hr) Stress at 100% elongation (MPa) 4.2 4.2 3.8 3.5 4.1 4.1 4.1 3.1 3.7 Elongation strength at break (MPa) 14.2 16.7 20.3 23.4 18.5 19.8 19.5 18.4 28.7 Elongation at break (%) 246 277 294 398 300 296 322 326 449 Rate of retention of elongation 0.45 0.52 0.60 0.86 0.60 0.65 0.58 0.87 0.84 strength at break Rate of preservation of elongation 0.49 0.57 0.65 0.80 0.65 0.65 0.63 0.82 0.84 at break Crack growth length (mm) 23 18 17 45 17 17 19 45 15 Comp. Ex. Comp. Ex. Comp. Ex. Comp. Ex. II-10 II-11 II-12 Ex. II-1 Ex. II-2 Ex. II-3 Ex. II-4 Ex. II-5 II-13 IR base master batch 155 155 155 155 155 155 155 155 155 Powdered sulfur — — 1.6 1.4 1.2 1.0 0.9 0.7 0.5 Vulcanization accelerator 1 (CBS) — — — — — — — — — Vulcanization accelerator 2 (TBBS) 1.0 — 1.8 1.73 1.67 1.6 1.57 1.5 1.43 Vulcanization accelerator 3 (MBTS) — 1.4 — — — — — — — Vulcanization accelerator 4 (TET) — — — — — — — — — Vulcanization accelerator 5 (DPG) — — — — — — — — — Vulcanization accelerator 6 (DOTU) — — — — — — — — — Polysulfide 1 3.0 3.5 0.6 1.0 1.4 1.8 2.0 2.4 2.8 Polysulfide 2 — — — — — — — — — Polysulfide 3 — — — — — — — — — Polysulfide 4 — — — — — — — — — Polysulfide 5 — — — — — — — — — Ratio of amount of polysulfide — — 0.36 0.71 1.17 1.8 2.22 3.43 5.6 added/amount of sulfur added Ratio by weight of (polysulfide + 3.0 2.5 1.22 1.38 1.56 1.75 1.65 2.07 2.30 sulfur)/accelerator VM (×10⁻⁵ mol/cc) 1.5 1.9 5.1 4.4 4.0 3.6 3.4 3.0 2.7 VD (×10⁻⁵ mol/cc) 4.0 6.3 5.1 5.3 5.6 5.7 5.7 5.8 5.9 VM + D (×10⁻⁵ mol/cc) 6.5 8.2 10.2 9.7 9.6 9.3 9.2 8.8 8.5 VT (×10⁻⁵ mol/cc) 15.4 14.6 15.8 16.3 16.7 17.1 17.4 17.8 18.3 VM/VT 0.10 0.13 0.32 0.27 0.24 0.21 0.20 0.17 0.15 VM/VD 0.38 0.30 0.99 0.82 0.71 0.63 0.60 0.52 0.45 (V − VM + D)/VT 0.58 0.44 0.35 0.40 0.42 0.46 0.47 0.50 0.53 Vulcanization time T₉₅ (150° C.) (min) 27.1 35.2 10.2 10.8 11.2 12.5 14.5 19.8 24.1 tanδ (60° C.) 0.145 0.149 0.121 0.122 0.124 0.126 0.136 0.151 0.159 (Not yet aged) Stress at 100% elongation (MPa) 2.9 2.8 3.0 3.1 3.2 3.3 3.3 3.4 3.5 Elongation strength at break (MPa) 33.5 30.1 31.7 31.2 31.0 30.9 31.1 30.6 31.5 Elongation at break (%) 532 509 492 498 508 512 509 521 532 Crack growth length (mm) 12 15 7 6 7 8 7 9 12 (Aged at 100° C. × 96 hr) Stress at 100% elongation (MPa) 3.8 3.6 4.3 4.3 4.3 4.4 4.5 4.5 4.5 Elongation strength at break (MPa) 28.1 25.3 19.7 22.2 22.3 23.2 23.3 24.5 26.5 Elongation at break (%) 447 428 285 349 366 379 387 412 431 Rate of retention of elongation 0.84 0.84 0.62 0.71 0.72 0.75 0.75 0.80 0.84 strength at break Rate of preservation of elongation 0.84 0.84 0.58 0.70 0.72 0.74 0.76 0.79 0.81 at break Crack growth length (mm) 13 16 Break 32 25 19 17 11 13 Comp. Ex. Comp. Ex. Comp. Ex. Comp. Ex. II-14 Ex. II-6 II-15 II-16 Ex. II-7 II-17 IR base master batch 155 155 155 155 155 155 Powdered sulfur 0.8 0.9 1.0 1.0 1.0 1.0 Vulcanization accelerator 1 (CBS) — — — — — — Vulcanization accelerator 2 (TBBS) 1.0 1.0 1.0 1.0 1.0 1.0 Vulcanization accelerator 3 (MBTS) — — — — — — Vulcanization accelerator 4 (TET) — — — — — — Vulcanization accelerator 5 (DPG) — — — — — — Vulcanization accelerator 6 (DOTU) — — — — — — Polysulfide 1 1.5 0.63 — — — — Polysulfide 2 — — 1.8 — — — Polysulfide 3 — — — 1.8 — — Polysulfide 4 — — — — 1.8 — Polysulfide 5 — — — — — 1.8 Ratio of amount of polysulfide 1.89 0.92 1.80 1.60 1.80 1.80 added/amount of sulfur added Ratio by weight of (polysulfide + 2.30 1.73 1.75 1.75 1.75 1.75 sulfur)/accelerator VM (×10⁻⁵ mol/cc) 2.8 2.5 2.6 9.1 3.3 2.4 VD (×10⁻⁵ mol/cc) 7.1 5.7 5.0 3.5 6.0 2.8 VM + D (×10⁻⁵ mol/cc) 9.9 6.2 7.6 12.6 9.3 5.2 VT (×10⁻⁵ mol/cc) 16.1 14.0 17.8 15.9 17.5 15.3 VM/VT 0.17 0.18 0.14 0.57 0.19 0.16 VM/VD 0.39 0.44 0.51 2.60 0.55 0.86 (VT − VM + D)/VT 0.39 0.42 0.57 0.21 0.47 0.66 Dispersion at roll mixing — — Good Good Good Good Vulcanization time T₉₅ (150° C.) 16.1 13.1 9.9 22.1 10.0 20.5 (min) tanδ (60° C.) 0.152 0.139 0.12 0.151 0.122 0.149 (Not yet aged) Stress at 100% elongation (MPa) 3.1 2.7 3.5 2.7 3.4 3 Elongation strength at break (MPa) 31.2 28.6 31.6 22.5 31.5 30.2 Elongation at break (%) 573 598 476 482 522 511 Crack growth length (mm) 8 4 9 Break 7 6 (Aged at 100° C. × 96 hr) Stress at 100% elongation (MPa) 4.1 3.6 5.1 3.2 4.6 4.5 Elongation strength at break (MPa) 25.6 21.5 16.4 18.0 23.9 18.1 Elongation at break (%) 476 454 271 371 397 322 Rate of retention of elongation 0.82 0.75 0.52 0.80 0.76 0.60 strength at break Rate of preservation of elongation 0.83 0.76 0.57 0.77 0.76 0.63 at break crack growth length (mm) 14 17 31 Break 17 25

[0214] Table II-1 Footnotes

[0215] Powdered sulfur: 5% oil extended sulfur

[0216] 1) Vulcanization Accelerator

[0217] Vulcanization accelerator 1 (CBS): N-cyclohexyl-2-benzothiazole sulfenamide

[0218] Vulcanization accelerator 2 (TBBS): N-t-butyl-2-benzothiazole sulfenamide

[0219] Vulcanization accelerator 3 (MBTS): dibenzothiazyl disulfide

[0220] Vulcanization accelerator 4 (TETD): tetraethylthiuram disulfide

[0221] Vulcanization accelerator 5 (DPG): diphenyl guanidine

[0222] Vulcanization accelerator 6 (DOTU): diorthotolylthiourea

[0223] 2) Polysulfide

[0224] Note) Samples with relatively low molecular weights can be measured for molecular weight, but rubbery high molecular weight sample cannot be obtained, and therefore, the Mooney viscosity is used instead.

[0225] Polysulfide 1 (4 Sulfur Atoms, Allyl End)

[0226] An excess of allyl chloride was added to a polysulfide polymer (Toray Thiokol, LP-32) in the presence of an equivalent amount of triethylamine to cause a reaction. The amine hydrochloride was filtered out, then the excess allyl chloride was distilled off. 36.2 g of powdered sulfur and 0.5 g of triethylamine were added to 100 g of this polymer and a reaction caused at 90° C. for 1 hour to obtain a viscous polysulfide polymer (average molecular weight of about 5500).

[0227] Polysulfide 2 (6 Sulfur Atoms, Allyl End)

[0228] An excess of allyl chloride was added to a polysulfide polymer (Toray Thiokol, LP-32) in the presence of an equivalent amount of triethylamine to cause a reaction. The amine hydrochloride was filtered out, then the excess allyl chloride was distilled off. 72.4 g of powdered sulfur and 0.5 g of triethylamine were added to 100 g of this polymer and a reaction caused at 90° C. for 1 hour to obtain a viscous polysulfide polymer (average molecular weight of about 7000).

[0229] Polysulfide 3 (2 Sulfur Atoms, Allyl End)

[0230] An excess of allyl chloride was added to a polysulfide polymer (Toray Thiokol, LP-31) in the presence of an equivalent amount of triethylamine to cause a reaction. The amine hydrochloride was filtered out, then the excess allyl chloride was distilled off to obtain a viscous polysulfide polymer (average molecular weight of about 8000).

[0231] Polysulfide 4 (4 Sulfur Atoms, Benzyl End)

[0232] An excess of benzyl chloride was added to a polysulfide polymer (Toray Thiokol, LP-31) in the presence of an equivalent amount of triethylamine to cause a reaction. The amine hydrochloride was filtered out, then the excess benzyl chloride was distilled off. 36.9 g of powdered sulfur and 0.5 g of triethylamine were added to 100 g of this polymer and a reaction caused at 90° C. for 1 hour to obtain a viscous polysulfide polymer (average molecular weight of about 11200).

[0233] Polysulfide 5 (4 Sulfur Atoms, Hydroxy End)

[0234] Three times the molar amount of ethylene oxide was reacted with a polysulfide polymer (Toray Thiokol, LP-32) in the presence of an alkali catalyst to convert the end to a hydroxyl group. 34.5 g of powdered sulfur and 0.5 g of triethylamine were added to 100 g of this polymer and a reaction caused at 90° C. for 3 hours to obtain a viscous polysulfide polymer (average molecular weight of about 5500).

[0235] Polysulfide Rubber 1 (4 Sulfur Atoms, End Alkyl) Mooney Viscosity of about 80)

[0236] 31.6 g of 1,2-dichloroethane, 2.69 g of benzyl chloride, 141 g of sodium tetrasulfide (41% solution), and 50 g of methanol were added and reacted at room temperature for 1 hour, then rinsed to obtain a rubbery polysulfide.

[0237] Polysulfide Rubber 2 (4 Sulfur Atoms, Mooney Viscosity of about 120)

[0238] 31.6 g of 1,2-dichloroethane, 135.5 g of sodium tetrasulfide (41%), and 50 g of methanol were used to obtain this in the same way as the polysulfide rubber 1.

[0239] Nipsil AQ: Nihon Silica Industry wet silica

[0240] Si69: Degussa silane coupling agent bis-(3-(triethoxysilyl)-propyl)tetrasulfide TABLE II-2 Comp. Comp. Comp. Ex. Ex. Ex. Ex. Ex. Ex. Ex. Ex. Ex. Ex. II-18 II-19 II-8 II-9 II-10 II-11 II-12 II-13 II-14 II-20 SBR base master batch 178 178 178 178 178 178 178 178 178 178 Powdered sulfur 1.5 1.3 1.2 1.0 0.9 0.9 0.8 0.6 0.6 0.4 Vulcanization accelerator 1 (CBS) — — — — — — — — — — Vulcanization accelerator 2 (TBBS) 1.4 1.46 1.49 1.28 1.0 1.0 1.33 1.29 1.29 1.15 Vulcanization accelerator 3 (MBTS) — — — — — — — — — — Vulcanization accelerator 4 (TET) — — — — — — — — — — Vulcanization accelerator 5 (DPG) — — — — — 0.4 — — 0.4 — Vulcanization accelerator 6 (DOTU) — — — — — — — — — — Polysulfide 1 — 0.49 0.86 0.83 0.83 0.83 1.6 2.06 2.06 2.24 Polysulfide 2 — — — — — — — — — — Polysulfide 3 — — — — — — — — — — Polysulfide 4 — — — — — — — — — — Polysulfide 5 — — — — — — — — — — Ratio of amount of polysulfide — 0.36 0.71 0.83 0.92 0.92 2.00 3.43 3.43 5.60 added/amount of sulfur added Ratio by weight of (polysulfide + — 1.22 1.38 1.43 1.73 1.73 1.60 2.07 2.07 2.30 sulfur)/accelerator VM (×10⁻⁵ mol/cc) 4.0 3.5 2.7 2.4 2.3 2.5 1.6 1.3 1.5 1.0 VD (×10⁻⁵ mol/cc) 1.7 1.7 2.0 1.9 2.2 2.1 2.7 3.0 3.0 3.2 VM + D (×10⁻⁵ mol/cc) 5.7 5.2 4.7 4.3 4.5 4.6 4.3 4.3 4.5 4.2 VT (×10⁻⁵ mol/cc) 11.6 11.3 11.1 11.1 11.1 11.3 11.3 11.2 11.2 11.5 VM/VT 0.34 0.31 0.24 0.22 0.21 0.22 0.14 0.12 0.13 0.09 VM/VD 2.35 2.06 1.35 1.26 1.05 1.19 0.59 0.43 0.50 0.31 (VT − VM + D)/VT 0.51 0.54 0.58 0.61 0.59 0.59 0.62 0.62 0.60 0.63 Vulcanization time T₉₅ (150° C.) 31.6 32.7 34.6 35.6 37.0 29.6 36.7 42.5 36.3 48.2 (min) tanδ (60° C.) 0.339 0.342 0.343 0.346 0.346 0.347 0.351 0.371 0.374 0.379 (Not yet aged) Stress at 100% elongation (MPa) 2.4 2.4 2.3 2.3 2.3 2.4 2.2 2.2 2.3 2.1 Elongation strength at break (MPa) 26.1 26.4 25.6 25.1 24.1 24.3 24 23.5 23.1 22.7 Elongation at break (%) 592 605 632 665 686 656 697 706 678 721 (Aged at 100° C. × 96 hr) Stress at 100% elongation (MPa) 3.4 3.3 3.2 3.1 3.0 3.1 2.8 2.7 2.8 2.5 Elongation strength at break (MPa) 17.0 17.4 17.9 18.3 18.1 16.7 18.5 18.8 18.9 19.1 Elongation at break (%) 355 375 442 479 515 499 537 579 570 620 Rate of retention of elongation 0.65 0.66 0.70 0.73 0.75 0.77 0.77 0.80 0.82 0.84 strength at break Rate of preservation of elongation 0.60 0.62 0.70 0.72 0.75 0.76 0.77 0.82 0.84 0.86 at break Comp. Comp. Comp. Ex. II-21 Ex. II-22 Ex. II-23 Ex. II-15 Ex. II-16 Ex. II-17 IR/BR base master batch MB1 MB2 MB3 MB1 MB2 MB3 Powdered sulfur 1.3 1.5 1.5 0.9 0.9 0.9 Vulcanization accelerator 2 (TBBS) 1.0 1.0 1.0 1.0 1.0 1.0 Polysulfide 1 (4 sulfur atoms, — — — 0.83 0.83 0.83 molecular weight 5500, end allyl) Ratio of amount of polysulfide — — — 0.92 0.92 0.92 added/amount of sulfur added Ratio by weight of (polysulfide + — — — 1.73 1.73 1.73 sulfur)/accelerator VM (×10⁻⁵ mol/cc) 2.2 2.1 2.0 2.5 2.4 2.4 VD (×10⁻⁵ mol/cc) 4.3 4.2 4.3 5.7 5.7 5.8 VM + D (×10⁻⁵ mol/cc) 6.5 6.3 6.3 8.2 8.1 8.2 VT (×10⁻⁵ mol/cc) 15.2 14.9 14.6 14.0 13.8 13.8 VM/VT 0.14 0.14 0.14 0.18 0.17 0.17 VM/VD 0.51 0.50 0.47 0.44 0.42 0.41 (VT − VM + D)/VT 0.57 0.58 0.57 0.42 0.41 0.41 Vulcanization time T₉₅ (150° C.) 10.0 10.2 10.7 13.5 13.8 13.9 (min) tanδ (60° C.) 0.124 0.115 0.103 0.138 0.129 0.118 (Not yet aged) Stress at 100% elongation (MPa) 2.7 2.4 2.3 2.7 2.4 2.3 Elongation strength at break (MPa) 30.1 29.8 28.3 28.6 28.5 27.9 Elongation at break (%) 497 489 479 598 581 573 (Aged at 100° C. × 96 hr) Stress at 100% elongation (MPa) 3.8 3.4 3.3 3.5 3.2 3.1 Elongation strength at break (MPa) 19.6 18.8 17.0 21.5 21.1 20.1 Elongation at break (%) 298 279 254 449 424 418 Rate of retention of elongation 0.65 0.63 0.60 0.75 0.74 0.72 strength at break Rate of preservation of elongation 0.60 0.57 0.53 0.75 0.73 0.73 at break Comp. Comp. Comp. Ex. II-24 Ex. II-25 Ex. II-26 Ex. II-18 Ex. II-19 Ex. II-20 IR (Nipol IR2200) 100 100 100 100 100 100 N339 carbon black 45 40 30 45 40 30 Silica (Nipsil AQ) 5 10 20 5 10 20 Silane coupling agent (Si69) 0.5 1 2 0.5 1 2 Diethylene glycol 0.25 0.5 1 0.25 0.5 1 Zinc white 3 3 3 3 3 3 Stearicacid 2 2 2 2 2 2 Antioxidant 6C 2 2 2 2 2 2 Powdered sulfur 1.3 1.5 1.5 0.9 0.9 0.9 Vulcanization accelerator 2 (TBBS) 1.0 1.0 1.0 1.0 1.0 1.0 Polysulfide 1 — — — 0.83 0.83 0.83 Ratio of amount of polysulfide — — — 0.92 0.92 0.92 added/amount of sulfur added Ratio by weight of (polysulfide + — — — 1.73 1.73 1.73 sulfur)/accelerator VM (×10⁻⁵ mol/cc) 2.2 2.0 1.9 2.5 2.6 2.8 VD (×10⁻⁵ mol/cc) 4.3 4.5 4.8 5.8 5.6 5.3 VM + D (×10⁻⁵ mol/cc) 6.5 6.5 6.7 8.3 8.2 9.1 VT (×10⁻⁵ mol/cc) 15.3 15.6 15.9 14.3 14.5 14.7 VM/VT 0.14 0.13 0.12 0.18 0.18 0.11 VM/VD 0.51 0.44 0.40 0.43 0.46 0.53 (VT − VM + D)/VT 0.58 0.56 0.58 0.42 0.43 0.45 Vulcanization time T₉₅ (150° C.) 11.5 13.6 14.3 14.5 14.8 15.1 (min) tanδ (60° C.) 0.12 0.116 0.103 0.131 0.127 0.112 (Not yet aged) Stress at 100% elongation (MPa) 2.8 2.9 3.1 2.7 2.9 3.0 Elongation strength at break (MPa) 30.1 29.8 28.3 28.6 28.5 27.9 Elongation at break (%) 481 468 451 572 553 542 (Aged at 100° C. × 96 hr) Stress at 100% elongation (MPa) 3.9 4.0 4.2 3.5 3.7 3.8 Elongation strength at break (MPa) 19.6 20.3 19.8 21.5 21.9 21.8 Elongation at break (%) 289 290 293 429 420 428 Rate of retention of elongation 0.65 0.68 0.70 0.75 0.77 0.78 strength at break Rate of preservation of elongation 0.60 0.62 0.65 0.75 0.76 0.79 at break Comp. Comp. Ex. II-27 Ex. II-21 Ex. II-22 Ex. II-28 IR base master batch 155 155 155 155 powdered sulfur 1.5 0.9 1.0 1.0 Vulcanization accelerator 2 (TBBS) 1.0 1.0 1.6 1.6 Polysulfide 1 — 0.83 — — Polysulfide rubber 1 — — 1.8 — Polysulfide rubber 2 — — — 1.8 N-(cyclohexylthio)phthalimide 0.2 0.2 — — (anti-scorch agent) Ratio of amount of polysulfide 1.5 0.92 1.8 1.8 added/amount of sulfur added Ratio by weight of (polysulfide + — 1.73 1.75 1.75 sulfur)/accelerator VM (×10⁻⁵ mol/cc) 2.1 1.9 3.4 2.6 VD (×10⁻⁵ mol/cc) 4 3.8 5.8 5.0 VM + D (×10⁻⁵ mol/cc) 6.1 6.7 9.2 7.6 VT (×10⁻⁵ mol/cc) 15.2 14.8 17.5 17.1 VM/VT 0.14 0.13 0.19 0.15 VM/VD 0.53 0.50 0.59 0.51 (VT − VM + D)/VT 0.60 0.61 0.47 0.55 Dispersion at roll mixing — — Good Poor Vulcanization time T₉₅ (150° C.) 12.2 14.1 10.2 11.1 (min) tanδ (60° C.) 0.121 0.137 0.126 0.127 (Not yet aged) Stress at 100% elongation (MPa) 3.1 2.9 3.3 3.1 Elongation strength at break (MPa) 31.1 27.9 30.9 28.7 Elongation at break (%) 506 612 512 501 Crack growth length (mm) — — 8 10 (Aged at 100° C. × 96 hr) Stress at 100% elongation (MPa) 4.2 2.9 4.4 4.3 Elongation strength at break (MPa) 15.9 20.3 23.2 19.9 Elongation at break (%) 296 478 379 342 Rate of retention of elongation 0.51 0.73 0.75 0.69 strength at break Rate of preservation of elongation 0.58 0.78 0.74 0.68 at break Crack growth length (mm) — — 19 28

Examples II-22 to II-25 and Comparative Examples II-26

[0241] Preparation of Samples

[0242] The ingredients of the SBR base master batch B of the following formulations (parts by weight) and the above-mentioned IR base master batch were mixed in a closed type mixer (i.e. Banbury mixer) for 3 to 5 minutes. The contents were discharged when reaching about 165° C. SBR base master batch (B) (parts by weight) Emulsion SBR (Styrene content = 35%, 70 Ave. Mw = 600,000) Solution SBR (Styrene content = 18%, 30 vinyl content = 8%, Ave. Mw = 500,000) N339 carbon black (Tokai Carbon, 75 Seast KH) Zinc white 3 Industrial use stearic acid 1 Oil 45 Antioxidant 6C*¹ 1 Total 225

[0243] The vulcanization agents and vulcanization accelerators (parts by weight) shown in Tables I to IV were kneaded into the master batches obtained by an open roll to obtain the rubber compositions.

[0244] Next, the rubber compositions obtained were press vulcanized in 15×15×0.2 cm molds at 160° C. for 20 minutes to prepare the desired test pieces-which were then evaluated as to vulcanized physical properties before and after aging (100° C.×96 hours). The resultant compositions are shown in Table II-6. TABLE II-6 Comp. Ex. Ex. Ex. Ex. Ex. II-28 II-22 II-23 II-24 II-25 SBR base master batch (B) 225 225 225 — — IR base master batch — — — 155 155 Powdered sulfur 17 0.9 — — — Vulcanization accelerator 1 (CBS) 2.5 1.6 3.3 — 3.0 Vulcanization accelerator 2 (TBBS) — — — 3.0 — Polysulfide 1 — 1.6 3.0 3.0 3.0 Ratio of amount of polysulfide — 1.78 — — — added/amount of accelerator added — 1.56 0.91 1.0 1.0 VM (×10⁻⁵ mol/cc) 2.7 2.8 2.7 3.1 4.0 VD (×10⁻⁵ mol/cc) 3.3 3.1 2.7 5.9 7.4 VM + D (×10⁻⁵ mol/cc) 6.0 5.9 5.4 9.0 11.4 VT (×10⁻⁵ mol/cc) 11.7 12.2 10.2 16.0 19.0 VM/VT 0.23 0.23 0.26 0.19 0.21 VM/VD 0.82 0.90 1.00 0.53 0.54 (VT − VM + D)/VT 0.49 0.52 0.47 0.44 0.40 Vulcanization Time T₉₅ (160° C.) 9.2 10.1 17.1 31.1 26.2 tanδ (60° C.) 0.243 0.236 0.245 0.132 0.133 (Not yet aged) Stress at 100% elongation (MPa) 1.9 2.1 1.9 2.8 2.7 Elongation strength at break (MPa) 19.7 20.0 19.4 32.1 31.0 Elongation at break (%) 550 547 560 502 511 Crack growth length (mm) — — — 9 8 (Aged at 100° C. × 96 hr) Stress at 100% elongation (MPa) 4.2 4.0 3.6 4.1 4.1 Elongation strength at break (MPa) 17.2 19.8 20.1 24.1 24.6 Elongation at break (%) 350 405 445 371 379 Retention rate of strength at 0.87 0.99 1.04 0.75 0.79 break Retention rate of elongation at 0.64 0.74 0.79 0.74 0.74 break Crack growth length (mm) — — — 20 19

Examples III-1 to III-13 and Comparative Examples III-1 to III-14

[0245] Preparation of Samples

[0246] The ingredients of the master batches of the following formulations (parts by weight) were mixed in a closed mixer for 3 to 5 minutes. The contents were discharged when reaching about 165° C. IR base master batch (parts by weight) IR (Nippon Zeon, Nipol IR 2200) 100 N339 carbon black (Tokai Carbon, Seast KH) 50 Zinc oxide (Zinc White No. 3) 3 Industrial use stearic acid 1 Antioxidant 6C*¹ 1 Total 155

[0247] SBR base master batch (parts by weight) SBR (Nippon Zeon, Nipol 1502) 100 N220 carbon black (Mitsubishi Chemical, 62 Diablack I) Zinc white 3 Stearic acid 1 Modified rosin resin 6 Oil 5 Antioxidant 6C*¹ 1 Total 178

[0248] The vulcanization agents and vulcanization accelerators (parts by weight) shown in Tables III-1 to III-3 were kneaded into the obtained master batches by an open roll to obtain the rubber compositions.

[0249] Next, the rubber compositions obtained were press vulcanized in 15×15×0.2 cm molds at 160° C. for 20 minutes to prepare the desired test pieces which were then evaluated as to vulcanized physical properties before and after aging (100° C.×96 hours). The resultant compositions are shown in Tables III-1 to III-3.

[0250] The test methods of the vulcanized physical properties were as follows:

[0251] Dispersion at time of roll mixing: The degree of mixing of the master batch and organic sulfur compound was judged visually.

[0252] Good: State where the master batch and organic sulfur compound are compatible and sufficiently mixed together

[0253] Poor: State where the organic sulfur compound is scattered in granular form and poor dispersion is caused

[0254] Reversion T-3 (160° C.): The time (minutes) when the torque falls 3% from the maximum torque (at 100% vulcanization) when measured at 160° C. based on JIS K6301 (Judged as “none” when torque does not fall within 45 minutes)

[0255] Vulcanization time T₉₅ (150° C.) (minutes): Time (minutes) until reaching 95% vulcanization degree at 150° C. based on JIS K6301

[0256] tan δ (60° C.): A Toyo Seiki Seisakusho viscoelasticity spectrometer (Rheorosolid) was used for measurement at an amplitude of +2% at 60° C., a frequency of 20 Hz, and an initial strain of 10%.

[0257] Strain at 100% elongation (MPa): Measured according to JIS K6301 (dumbbell type No. 3)

[0258] Elongation strength at break (MPa): Measured according to JIS K6301 (dumbbell type No. 3)

[0259] Elongation at break (%): Measured according to JIS K6301 (dumbbell type No. 3)

[0260] Table I Footnotes

[0261] 1) Vulcanization Accelerator

[0262] Vulcanization accelerator 1 (CBS): N-cyclohexyl-2-benzothiazole sulfenamide

[0263] Vulcanization accelerator 2 (TBBS): N-t-butyl-2-benzothiazole sulfenamide

[0264] Vulcanization accelerator 3 (MBTS): dibenzothiazyl sulfide

[0265] Vulcanization accelerator 4 (DPG): diphenyl guanidine

[0266] Note) Samples with relatively low molecular weights can be measured for molecular weight, but rubbery ones with high weights cannot, so the Mooney viscosity is used instead.

[0267] 2) Preparation of Polysulfide

[0268] Polysulfide 1 (4 Sulfur Atoms, Allyl End)

[0269] An excess of allyl chloride was added to a polysulfide polymer (Toray Thiokol, LP-32) in the presence of an equivalent amount of triethylamine to cause a reaction. The amine hydrochloride was filtered out, then the excess allyl chloride was distilled off. 36.2 g of powdered sulfur and 0.5 g of triethylamine were added to 100 g of this polymer and a reaction caused at 90° C. for 1 hour to obtain a viscous polysulfide polymer (average molecular weight of about 5500).

[0270] Polysulfide 2 (6 Sulfur Atoms, Allyl End)

[0271] An excess of allyl chloride was added to a polysulfide polymer (Toray Thiokol, LP-32) in the presence of an equivalent amount of triethylamine to cause a reaction. The amine hydrochloride was filtered out, then the excess allyl chloride was distilled off. 72.4 g of powdered sulfur and 0.5 g of triethylamine were added to 100 g of this polymer and a reaction caused at 90° C. for 1 hour to obtain a viscous polysulfide polymer (average molecular weight of about 7000).

[0272] Polysulfide 3 (2 Sulfur Atoms, Allyl End)

[0273] An excess of allyl chloride was added to a polysulfide polymer (Toray Thiokol, LP-31) in the presence of an equivalent amount of triethylamine to cause a reaction. The amine hydrochloride was filtered out, then the excess allyl chloride was distilled off to obtain a viscous polysulfide polymer (average molecular weight of about 8000).

[0274] Polysulfide 4 (4 Sulfur Atoms, Benzyl End)

[0275] An excess of benzyl chloride was added to a polysulfide polymer (Toray Thiokol, LP-31) in the presence of an equivalent amount of triethylamine to cause a reaction. The amine hydrochloride was filtered out, then the excess benzyl chloride was distilled off. 36.9 g of powdered sulfur and 0.5 g of triethylamine were added to 100 g of this polymer and a reaction caused at 90° C. for 1 hour to obtain a viscous polysulfide polymer (average molecular weight of about 11200).

[0276] Polysulfide 5 (4 Sulfur Atoms, Hydroxy End)

[0277] Three times the molar amount of ethylene oxide was reacted with a polysulfide polymer (Toray Thiokol, LP-32) in the presence of an alkali catalyst to convert the end to a hydroxyl group. 34.5 g of powdered sulfur and 0.5 g of triethylamine were added to 100 g of this polymer and a reaction caused at 90° C. for 3 hours to obtain a viscous polysulfide polymer (average molecular weight of about 5500).

[0278] Polysulfide rubber 1 (4 Sulfur Atoms, End Alkyl, Mooney Viscosity of about 80)

[0279] 31.6 g of 1,2-dichloroethane, 2.69 g of benzyl chloride, 141 g of sodium tetrasulfide (41% solution), and 50 g of methanol were added and reacted at room temperature for 1 hour, then rinsed to obtain a rubbery polysulfide.

[0280] Polysulfide Rubber 2 (4 Sulfur Atoms, Mooney Viscosity of about 120)

[0281] 31.6 g of 1,2-dichloroethane, 135.5 g of sodium tetrasulfide (41%), and 50 g of methanol were used to obtain this in the same way as the polysulfide rubber 1. TABLE III-1 Comp. Comp. Comp. Comp. Comp. Comp. Ex. Ex. Ex. Ex. Ex. Ex. Ex. Ex. Ex. Ex. III-1 III-2 III-3 III-5 III-1 III-2 III-3 III-6 III-4 III-7 IR base master batch 155 155 155 155 155 155 155 155 155 155 Powdered sulfur 1.5 1.5 2.0 1.5 1.35 1.25 1.2 1.1 1.25 1.1 Vulcanization accelerator 1 (CBS) 1.2 — — — — — — — 1.2 1.2 Vulcanization accelerator 2 (TBBS) — 1.0 — 1.0 1.0 1.0 1.0 1.0 — — Vulcanization accelerator 3 (MBTS) — — 1.4 — — — — — — — Vulcanization accelerator 4 (DPG) — — — 0.2 — — — — — — Polysulfide 1 — — — — 0.3 0.5 0.6 0.8 0.5 0.8 Polysulfide 2 — — — — — — — — — — Polysulfide 3 — — — — — — — — — — Polysulfide 4 — — — — — — — — — — Polysulfide 5 — — — — — — — — — — Ratio of amount of polysulfide — — — — 0.22 0.4 0.5 0.73 0.4 0.73 added/amount of sulfur added Reversion T-30 (160° C.) 32.0 35.2 41.5 31.2 None None None None None None Vulcanization time T₉₅ (150° C.) 9.2 10.1 14.1 8.5 10.1 10.2 10.4 12.1 9.4 10.1 tanδ (60° C.) 0.124 0.120 0.136 0.122 0.121 0.122 0.123 0.130 0.124 0.136 Stress at 100% elongation (MPa) 2.9 2.9 2.9 2.9 2.9 2.9 2.9 2.7 2.9 2.8 Elongation strength at break (MPa) 31.5 32.1 33.8 30.9 32.2 32.3 32.1 33.1 31.3 33.2 Elongation at break (%) 502 486 4S2 462 489 487 490 507 503 515 Comp. Comp. Comp. Comp. Ex. Ex. Ex. Ex. Ex. Ex. Ex. Ex. Ex. III-5 III-8 III-6 III-7 III-8 III-9 III-10 III-9 III-11 IR base master batch 155 155 155 155 155 155 155 155 155 Powdered sulfur 1.7 1.5 1.25 1.25 1.25 1.25 1.25 1.25 1.25 Vulcanization accelerator 1 (CBS) — — — 1.2 — — — — — Vulcanization accelerator 2 (TBBS) — — 1.0 — 1.0 1.0 1.0 1.0 1.0 Vulcanization accelerator 3 (MBTS) 1.4 1.4 — — — — — — — Vulcanization accelerator 4 (DPG) — — 0.2 0.2 — — — — — Polysulfide 1 0.6 1.0 0.5 0.5 0.5 — — — — Polysulfide 2 — — — — — 0.5 — — — Polysulfide 3 — — — — — — 0.5 — — Polysulfide 4 — — — — — — — 0.5 — Polysulfide 5 — — — — — — — — 0.5 Ratio of amount of polysulfide 0.35 0.67 0.4 0.4 0.4 0.4 0.4 0.4 0.4 added/amount of sulfur added Dispersion at roll mixing — — — — Good Good Good Good Good Reversion T-30 (160° C.) None None None None None 43.0 None None None Vulcanization time T₉₅ (150° C.) 14.5 15.6 8.6 7.1 10.2 9.8 11.5 10.3 12.6 tanδ (60° C.) 0.138 0.149 0.123 0.125 0.122 0.121 0.131 0.123 0.132 Stress at 100% elongation (MPa) 3.0 3.1 2.9 3.0 2.9 3.1 2.7 2.9 2.6 Elongation strength at break (MPa) 33.1 334.2 31.1 32.3 32.3 32.8 30.3 32.1 29.5 Elongation at break (%) 457 470 468 475 487 467 501 485 511

[0282] TABLE III-2 Comp. Ex. Ex. Ex. III-12 III-10 III-11 SBR base master batch 178 178 178 Powdered sulfur 1.5 1.25 1.0 Vulcanization accelerator 2 (TBBS) 1.4 1.4 1.4 Vulcanization accelerator 4 (DPG) — — — Polysulfide 1 — 0.5 1.0 Ratio of amount of polysulfide — 0.4 1.0 added/amount of sulfur added Reversion T-30 (160° C.) 48.3 None None Vulcanization time T₉₅ (150° C.) 21.6 32.8 34.6 tanδ (60° C.) 0.339 0.34 0.356 Stress at 100% elongation (MPa) 2.4 2.4 2.3 Elongation strength at break (MPa) 26.1 26.4 25.6 Elongation at break (%) 592 599 621

[0283] TABLE III-3 Comp. Comp. Ex. Ex. Ex. Ex. III-13 III-12 III-13 III-14 IR base master batch 155 155 155 155 Powdered sulfur 1.5 1.25 1.25 1.25 Vulcanization accelerator 2 1.0 1.0 1.0 1.0 (TBBS) Polysulfide 1 — 0.5 — — Polysulfide rubber 1 — — 0.50 — Polysulfide rubber 2 — — — 0.55 N-(cyclohexylthio) 0.2 0.2 — — phthalimide Ratio of amount of — 0.4 0.4 0.4 polysulfide added/amount of sulfur added Dispersion at roll mixing Good Good Good Poor Reversion T-30 (160° C.) 35.2 None None None Vulcanization time T₉₅ 10.1 10.3 10.0 10.5 (150° C.) tanδ (60° C.) 0.120 0.123 0.120 0.121 Stress at 100% elongation 2.9 2.8 3.1 2.7 (MPa) Elongation strength at break 32.1 32.5 32.9 29.1 (MPa) Elongation at break (%) 486 492 488 456 # polymer and a reaction caused at 90° C. for 1 hour to obtain a viscous polysulfide (average molecular weight of about 5500). # filter, and the crystals were washed further by distilled water several times and then dried to obtain the target compound.

[0284] The results of elementary analysis of the compound obtained (figures in parentheses shown theoretical values) were as follows:

[0285] C: 46.25% (46.13%), H: 2.22% (2.21%), N: 7.62% (7.68%), S: 43.91% (43.98%)

[0286] Test Methods

[0287] Tensile properties: Measured according to JIS K6251

[0288] Hardness (Hs): Measured according to JIS K6253 at 20° C.

[0289] tan δ: Measured using a Toyo Seiki Seisakusho viscoelasticity spectrometer at a static strain of 10%, a dynamic strain of ±2%, and a frequency of 20 Hz.

[0290] Abrasion resistance: Measured using a Lambourn abrasion tester (made by Iwamoto Seisakusho) under conditions of a load of 5 kg, a slip of 25%, a time of 4 minutes, and room temperature with the amount of abrasion loss indicated as an index. Note that the larger the value, the better the abrasion resistance shown.

Standard Example IV-1 and Examples IV-1 to IV-6

[0291] Preparation of Samples

[0292] The ingredients other than the sulfur compound and the vulcanization accelerator in each of the formulations (parts by weight) shown in Table IV-1 were kneaded by a Banbury mixer for 4 minutes and the contents discharged when reaching about 160° C. The sulfur compound and vulcanization accelerator shown in Table IV-1 were mixed into the master batch obtained by an open roll to obtain a rubber composition. The unvulcanized physical properties and the vulcanized physical properties of the obtained rubber composition were measured. The resultant compositions are shown in Table IV-1.

[0293] Preparation of Test Pieces

[0294] The obtained rubber compositions were press vulcanized in predetermined molds at 150° C. for 45 minutes to prepare the desired test pieces. TABLE IV-1 Standard Ex. IV-5 Ex. IV-1 Ex. IV-2 Ex. IV-3 Ex. IV-4 Ex. IV-5 Ex. IV-6 SBR 1502*² 100.0 100.0 100.0 100.0 100.0 100.0 100.0 N220 carbon black*⁵ 60.0 60.0 60.0 60.0 60.0 60.0 60.0 Resin 1*⁸ 5.0 5.0 5.0 5.0 5.0 5.0 5.0 Antioxidant 6PPD*¹¹ 2.0 2.0 2.0 2.0 2.0 2.0 2.0 Antioxidant RD*¹² 2.0 2.0 2.0 2.0 2.0 2.0 2.0 Wax*¹³ 2.0 2.0 2.0 2.0 2.0 2.0 2.0 Stearic acid*¹⁴ 1.0 1.0 1.0 1.0 1.0 1.0 1.0 Zinc white*¹⁵ 3.0 3.0 3.0 3.0 3.0 3.0 3.0 Aromatic oil*¹⁶ 5.0 5.0 5.0 5.0 5.0 5.0 5.0 Vulcanization accelerator NS*¹⁷ 1.4 1.4 1.4 1.4 1.4 1.4 1.4 Vulcanization accelerator DPG*¹⁸ — — — — 0.05 0.1 0.2 5% oil extended sulfur*¹⁸ 1.5 1.0 0.5 — 1.0 1.0 1.0 Sulfur compound 1*²⁰ — 0.83 1.67 2.5 0.83 0.83 0.83 (converted to amount of effective (1.4) (1.4) (1.3) (1.3) (1.4) (1.4) (1.4) sulfur) Tensile properties* BL 8.7 8.7 8.6 8.6 8.6 8.8 9.0 300% MOD TB 23.0 22.8 22.5 22.0 23.0 23.8 24.8 EB 691 681 679 670 678 687 675 AG 11.6 11.2 11.0 11.2 11.3 11.6 11.4 300% MOD TB 22.3 21.8 21.4 20.7 21.9 22.6 23.5 EB 550 571 578 591 577 597 607 Drop in LB after aging 141 110 101 79 101 90 88 ΔEB Hs (20° C.) 68 68 67 67 68 69 69 tanδ (60° C.) 0.307 0.308 0.307 0.312 0.308 0.307 0.309 Abrasion resistance (index) 100 105 120 156 106 103 105

Standard Example IV-2 and Examples IV-7 to IV-9

[0295] Preparation of Samples

[0296] The ingredients other than the sulfur compound and the vulcanization accelerator in each of the formulations (parts by weight) shown in Table IV-2 were mixed by a Banbury mixer for 4 minutes and the contents discharged when reaching about 160° C. The sulfur compound and vulcanization accelerator shown in Table IV-2 were kneaded into the master batch obtained by an open roll to obtain a rubber composition. The unvulcanized physical properties and the vulcanized physical properties of the obtained rubber composition were measured. The results are shown in Table IV-2.

[0297] Preparation of Test Pieces

[0298] The obtained rubber compositions were press vulcanized in predetermined molds at 150° C. for 45 minutes to prepare the desired test pieces. TABLE IV-2 Standard Ex. Ex. Ex. Ex. IV-2 IV-7 IV-8 IV-9 NR*¹ 100.0 100.0 100.0 100.0 N220 carbon black*⁵ 20.0 20.0 20.0 20.0 N330 carbon black*⁶ 20.0 20.0 20.0 20.0 Silica*⁷ 5.0 5.0 5.0 5.0 Resin 2*⁹ 5.0 5.0 5.0 5.0 Antioxidant 6PPD*¹¹ 2.0 2.0 2.0 2.0 Antioxidant RD*¹² 2.0 2.0 2.0 2.0 Wax*¹³ 2.0 2.0 2.0 2.0 Stearic acid*¹⁴ 1.0 1.0 1.0 1.0 Zinc white*¹⁵ 3.0 3.0 3.0 3.0 Aromatic oil*^(l6) 1.0 1.0 1.0 1.0 Vulcanization accelerator NS*¹⁷ 1.1 1.1 1.1 1.1 Vulcanization accelerator DPG*¹⁸ — — 0.2 0.2 5% oil extended sulfur*¹⁹ 1.5 1.0 1.0 — Sulfur compound 1*²⁰ — 0.83 0.83 2.5 (converted to amount of (1.4) (1.4) (1.4) (1.3) effective sulfur) Tensile properties* BL 9.5 9.5 9.8 9.4 300% MOD TB 26.5 26.4 28.4 25.6 EB 582 572 566 561 AG 11.6 11.2 11.4 11.2 300% MOD TB 25.5 25.0 26.7 23.9 EB 498 519 545 539 Drop in EB after aging 84 53 21 22 ΔEB Hs (20° C.) 55 55 56 54 tanδ (60° C.) 0.143 0.144 0.145 0.148 Abrasion resistance (index) 100 108 110 162

ΔEB=BL−AG

Standard Examples IV-3 and IV-4 and Examples IV-10 to IV-12

[0299] Preparation of Samples

[0300] The ingredients other than the sulfur compound and the vulcanization accelerator in each of the formulations (parts by weight) shown in Table IV-3 were kneaded by a Banbury mixer for 4 minutes and the contents discharged when reaching about 160° C. The sulfur compound and vulcanization accelerator shown in Table IV-3.were kneaded into the obtained master batch by an open roll to obtain a rubber composition. The unvulcanized physical properties and the vulcanized physical properties of the obtained rubber composition were measured. The results are shown in Table IV-3.

[0301] Preparation of Test Pieces

[0302] The obtained rubber compositions were press vulcanized in predetermined molds at 150° C. for 45 minutes to prepare the desired test pieces. TABLE IV-3 Standard Standard Ex. IV-3 Ex. IV-10 Ex. IV-11 Ex. IV-4 Ex. IV-12 NR*1 70.0 70.0 70.0 55.0 55.0 SBR 1502*2 — — — 22.0 22.0 BR 1220*3 30.0 30.0 30.0 23.0 23.0 N110 carbon black*4 — — — 50.0 50.0 N220 carbon black*5 50.0 50.0 50.0 — — Resin 3*10 2.0 2.0 2.0 2.0 2.0 Antioxidant 6PPD*11 2.0 2.0 2.0 2.0 2.0 Antioxidant RD*12 2.0 2.0 2.0 2.0 2.0 Wax*13 2.0 2.0 2.0 2.0 2.0 Stearic acid*14 1.0 1.0 1.0 1.0 1.0 Zinc white*15 3.0 3.0 3.0 3.0 3.0 Aromatic oil*16 3.0 3.0 3.0 1.0 1.0 Vulcanization 1.2 1.2 1.2 1.0 1.0 accelerator NS*17 Vulcanization — — 0.2 — accelerator DPG*18 5% oil extended 1.5 1.0 1.0 1.2 — sulfur*19 Sulfur compound 1*20 — 0.83 0.83 — 2.0 (converted to amount of (1.4) (1.4) (1.4) (1.1) (1.0) effective sulfur) Tensile properties* BL 11.4 11.0 11.5 10.6 10.1 300% MOD TB 26.5 26.4 27.0 22.4 23.0 EB 552 550 566 512 524 AG 12.6 12.1 12.5 11.6 11.2 300% MOD TB 23.5 23.0 24.0 20.1 21.0 EB 513 525 545 452 488 Drop in EB after aging 39 25 21 60 36 ΔEB Hs (20° C.) 62 61 62 65 65 tanδ (60° C.) 0.181 0.185 0.180 0.185 0.190 Abrasion resistance 100 110 115 100 148 (index)

Standard Example IV-5 and Examples IV-13 to IV-15

[0303] Preparation of Samples

[0304] The ingredients other than the sulfur compound and the vulcanization accelerator in each of the formulations (parts by weight) shown in Table IV-4 were mixed by a Banbury mixer for 4 minutes and the contents discharged when reaching about 160° C. The sulfur compound and vulcanization accelerator shown in Table IV-4 were mixed into the master batch obtained by an open roll to obtain a rubber composition. The unvulcanized physical properties and the vulcanized physical properties of the obtained rubber composition were measured. The resultant compositions are shown in Table IV-4.

[0305] Preparation of Test Pieces

[0306] The obtained rubber compositions were press vulcanized in predetermined molds at 150° C. for 45 minutes to prepare the desired test pieces. TABLE IV-4 Comp. Ex. Ex. Ex. Ex. IV-5 IV-13 IV-14 IV-15 SBR 1502*2 100.0 100.0 100.0 100.0 N220 carbon black*5 60.0 60.0 60.0 60.0 Resin 1*8 5.0 5.0 5.0 5.0 Antioxidant 6PPD*11 2.0 2.0 2.0 2.0 Antioxidant RD*12 2.0 2.0 2.0 2.0 Wax*13 2.0 2.0 2.0 2.0 Stearic acid*14 1.0 1.0 1.0 1.0 Zinc white*15 3.0 3.0 3.0 3.0 Aromatic oil*16 5.0 5.0 5.0 5.0 Vulcanization accelerator 1.4 1.4 1.4 1.4 NS*17 5% oil extended sulfur*18 1.5 1.0 0.5 — Sulfur compound 2*20 — 0.83 1.67 2.5 (converted to amount of (1.4) (1.3) (1.2) (1.1) effective sulfur) Tensile properties (148° C. × 45 min)* BL 8.7 8.5 8.0 7.9 300% MOD TB 23.0 22.8 22.5 22.0 EB 691 681 690 701 AG 11.6 10.8 10.1 9.4 300% MOD TB 22.3 21.8 21.4 20.7 EB 550 585 601 630 Drop in EB after aging 141 96 89 71 ΔEB Tensile properties (160° C. × 45 min)* BL 7.9 7.7 7.3 7.1 300% MOD TB 21.4 23.4 23.8 23.8 EB 706 710 740 750 AG 12.2 11.4 11.1 11.0 300% MOD TB 21.5 22.4 22.6 22.4 EB 538 612 650 676 Drop in EB after aging 168 98 90 74 ΔEB Hs (20° C.) 68 68 68 67 tanδ (60° C.) 0.307 0.312 0.315 0.322 Abrasion resistance (index) 100 121 141 156

Standard Examples IV-6 to IV-8 and Examples IV-16 to IV-18

[0307] Preparation of Samples

[0308] The ingredients other than the sulfur compound and the vulcanization accelerator in each of the formulations (parts by weight) shown in Table IV-5 were mixed by a Banbury mixer for 4 minutes and the contents discharged when reaching about 160° C. The sulfur compound and vulcanization accelerator shown in Table IV-5 were kneaded into the master batch obtained by an open roll to obtain a rubber composition. The unvulcanized physical properties and the vulcanized physical properties of the obtained rubber composition were measured. The resultant compositions are shown in Table IV-5.

[0309] Preparation of Test Pieces

[0310] The obtained rubber compositions were press vulcanized in predetermined molds at 150° C. for 45 minutes to prepare the desired test pieces. TABLE IV-5 Standard Standard Standard Ex. IV-6 Ex. IV-16 Ex. IV-7 Ex. IV-17 Ex. IV-8 Ex. IV-18 NR*1 100.0 100.0 70.0 70.0 55.0 55.0 SBR 1502*2 — — — — 22.0 22.0 BR1220*3 — — 30.0 30.0 23.0 23.0 N110 carbon black*4 — — — — 50.0 50.0 N220 carbon black*5 20.0 20.0 50.0 50.0 — — N330 carbon black*6 20.0 — — — — — Silica*7 5.0 — — — — — Resin 2*8 5.0 5.0 2.0 2.0 2.0 2.0 Antioxidant 6PPD*11 2.0 2.0 2.0 2.0 2.0 2.0 Antioxidant RD*12 2.0 2.0 2.0 2.0 2.0 2.0 Wax*13 2.0 2.0 2.0 2.0 2.0 2.0 Stearic acid*14 1.0 1.0 1.0 1.0 1.0 1.0 Zinc white*15 3.0 3.0 3.0 3.0 3.0 3.0 Aromatic oil*16 1.0 1.0 3.0 3.0 1.0 1.0 Vulcanization 1.1 1.1 1.2 1.2 1.0 1.0 accelerator NS*17 5% oil extended 1.5 — 1.5 1.0 1.2 — sulfur*18 Sulfur compound 2*21 — 2.5 — 0.83 — 2.0 (converted to amount (1.4) (1.1) (1.4) (1.3) (1.1) (0.9) of effective sulfur) Tensile properties (148° C. × 45 min)* BL 9.5 8.6 11.4 10.4 10.6 10.1 300% MOD TB 26.5 26.0 26.5 25.4 22.4 21.8 EB 582 592 552 550 512 516 AG 11.6 9.8 12.6 11.2 11.6 10.8 300% MOD TB 25.5 24.5 23.5 22.8 20.1 19.8 EB 498 550 513 535 452 488 Drop in EB after aging 84 42 39 15 60 28 ΔEB Tensile properties (160° C. × 45 min)* BL 300% MOD 8.6 8.4 10.4 9.8 10.0 10.4 TB 24.8 25.5 25.4 26.4 21.8 23.0 EB 552 584 532 570 498 524 AG 12.4 11.2 13.8 12.1 12.8 1.0 300% MOD TB 23.8 25.0 22.8 23.0 19.8 21.0 EB 470 538 480 552 434 489 Drop in EB after aging 82 46 52 18 64 35 ΔEB Hs (20° C.) 55 54 62 62 65 64 tanδ (60° C.) 0.143 0.160 0.181 0.190 0.185 0.194 Abrasion resistance 100 142 100 162 100 148 (index)

[0311] As explained above, according to the present invention, it is possible to suppress a decline in physical properties after heat aging without reducing the strength or elongation at break of the vulcanized rubber. Further, according to the present invention, it is possible to maintain the properties even after aging without reducing the repeated fatigue strength and, further, possible to shorten the vulcanization time drastically compared with known polysulfide rubber formulations.

[0312] In addition, according to the present invention, it is possible to improve the reversion resistance without changing the strength or elongation at break, the vulcanization time, the heat buildup property, and other physical properties of the vulcanized rubber.

[0313] Furthermore, according to the present invention, by compounding a sulfur compound having a specific structure (I) or (II) to a diene rubber, it is possible to obtain a rubber composition improved in abrasion resistance, heat aging characteristics (AEB), and appearance after use (EB after aging) while securing the heat buildup property and cut resistance (Hs, EB) when new (BL). 

1. A vulcanized rubber composition comprising a vulcanizable rubber, a reinforcing filler, and a sulfur compound having the formula (I): —(S_(x)R¹)_(n)—  (I) wherein R¹ represents an organic group, x is an average number of 3 to 5, and n is an integer of 1 to 100, wherein a ratio (VM/VD) is not more than 0.4, in which: a value VM is obtained from the degree of change before and after toluene swelling of the vulcanized rubber composition treated in a lithium aluminum hydride saturated tetrahydrofuran/toluene (ratio by volume 1/1) mixed solution using the formula (A): $\begin{matrix} {{{VM} = {{{- \frac{1}{Vs}} \cdot \left\lbrack \frac{{{\ln \left( {1 - {vr}_{M}} \right)} + {vr}_{M} + \mu}{\cdot {vr}_{M}^{2}}}{{vr}_{M}^{1/3} - {{vr}_{M}/2}} \right\rbrack}\quad {wherein}}}{{vr}_{M} = \frac{1 - \varphi}{X_{M} - \varphi}}} & (A) \end{matrix}$

wherein X_(M) is the degree of change before and after toluene swelling (volume after toluene swelling/volume before toluene swelling)after treatment in a lithium aluminum hydride saturated tetrahydrofuran/toluene (ratio by volume 1/1) mixed solution, φ is the volume percentage of the reinforcing filler in the rubber composition, V_(s) is the molecular volume of toluene, μ is the rubber•toluene interaction coefficient, and vr_(M) is the volume percentage of rubber in the swelled rubber after treatment in a lithium aluminum hydride saturated tetrahydrofuran/toluene (ratio by volume 1/1) mixed solution) and a value VD is obtained from the degree of change before and after toluene swelling of the vulcanized rubber composition treated in a propane-2-thiol (0.4 mol/l)/piperidine (0.4 mol/1) added tetrahydrofuran/toluene (ratio by volume 1/1) mixed solution using the formula (B): $\begin{matrix} \begin{matrix} {{VD} = {{- \frac{1}{Vs}} \cdot \left\lbrack {\frac{{\ln \left( {1 - {vr}_{D + M}} \right)} + {vr}_{D + M} + {\mu \cdot {vr}_{D + M}^{2}}}{{vr}_{D + M}^{1/3} - {{vr}_{D + M}/2}} -} \right.}} \\ {{\left. \frac{\left. {{\ln \left( {1 - {vr}_{M}} \right)} + {vr}_{M}} \right) + {\mu \cdot {vr}_{M}^{2}}}{{vr}_{M}^{1/3} - {{vr}_{M}/2}} \right\rbrack}\quad {wherein}} \\ {{{vr}_{D + M} = \frac{1 - \varphi}{x_{D + M} - \varphi}}} \end{matrix} & (B) \end{matrix}$

wherein X_(D+M) is the degree of change before and after toluene swelling (volume after toluene swelling/volume before toluene swelling)after treatment in a propane-2-thiol (0.4 mol/l)/piperidine (0.4 mol/l) added tetrahydrofuran/toluene (ratio by volume 1/1) mixed solution and vr_(D+M) is the volume percentage of rubber in the swelled rubber after treatment in a propane-2-thiol (0.4 mol/l)/piperidine (0.4 mol/l) added tetrahydrofuran/toluene (ratio by volume 1/1) mixed solution
 2. A vulcanized rubber composition as claimed in claim 1, wherein the ratio (VM/VT) is not more than 0.15, in which VT is obtained from the degree of change before and after toluene swelling of the untreated vulcanized rubber composition using formula (C): $\begin{matrix} {{{VT} = {{{- \frac{1}{Vs}} \cdot \left\lbrack \frac{{\ln \left( {1 - {vr}_{T}} \right)} + {vr}_{T} + {\mu \cdot {vr}_{T}^{2}}}{{vr}_{T}^{1/3} - {{vr}_{T}/2}} \right\rbrack}\quad {wherein}}}{{vr}_{T} = \frac{1 - \varphi}{X_{T} - \varphi}}} & (C) \end{matrix}$

wherein X_(T) is the degree of change before and after toluene swelling when untreated (volume after toluene swelling/volume before toluene swelling) and vr_(T) is the volume percentage of rubber in the swelled rubber when untreated.
 3. A rubber composition as claimed in claim 1, wherein the Mooney viscosity of the material of the sulfur compound is not more than
 100. 4. A vulcanized rubber composition as claimed in claim 1, wherein the sulfur compound is a polysulfide polymer having a number average molecular weight of 200 to
 15000. 5. A vulcanized rubber composition as claimed in claim 1, wherein the sulfur compound is a polysulfide polymer having the formula (III) to which sulfur is added in the backbone and having y of 3 to 5 on average and z of 3 to 5 on average: R³S_(z)R²(S_(y)R²)_(m)S_(z)R³  (III) wherein R² is a C₂ to C₁₀ oxyalkylene group and/or C₂ to C₁₀ and O₂ to O₁₀, polyoxyalkylene group, R is at least one functional group selected from the group consisting of a C₁ to C₃₀ hydrocarbon group, y is a number of 1.0 to 6.0, z is a number of 1.0 to 6.0, and m is an integer of 1 to 50, wherein the polysulfide polymer has an R² of formula (III) shown by the following formula (IV): —C₂H₄OC_(m′)H_(2m′)OC₂H₄—  (IV) wherein m′ is an integer of 1 to
 2. 6. A vulcanized rubber composition as claimed in claim 1, wherein at least one vulcanization accelerator selected from the group consisting of a thiazole base, sulfenamide base, thiuram base, and dithio acid salt base accelerators is compounded into 0.5 to 5 parts by weight of the polysulfide polymer so as to give a ratio by weight of the vulcanization accelerator and the polysulfide polymer of 0.3 to
 4. 7. A vulcanized rubber composition as claimed in claim 1, wherein at least one vulcanization accelerator selected from the group consisting of a guanidine base, aldehyde-ammonia base, aldehyde-amine base, and thiourea base accelerators is compounded in an amount of 0.05 to 1 part by weight based upon 100 parts by weight of the starting rubber.
 8. A vulcanized rubber composition comprising 100 parts by weight of a vulcanizable rubber, a reinforcing filler, and a sulfur compound (1) having the formula (I): —(S_(x)R¹)—  (I) wherein, R¹ represents an organic group, x is an average number of 3 to 5, and n is an integer of 1 to 100 in an amount of not more than 20 parts by weight, or the sulfur compound (1) and sulfur (2) in a ratio by weight (1)/(2) of at least 0.5 and in a total weight of (1)+(2) of not more than 20 parts by weight, vulcanized by compounding at least one vulcanization accelerator (3) selected from the group consisting of a thiazole base, sulfenamide base, thiuram base, and diothio acid base accelerators in an amount so as to give a ratio by weight [(1)+(2)]/(3) of not more than 2.2, wherein a value VM is obtained from the degree of change before and after toluene swelling of the vulcanized rubber composition treated in a lithium aluminum hydride saturated tetrahydrofuran/toluene (ratio by volume 1/1) mixed solution using the formula (A): $\begin{matrix} {{{VM} = {{{- \frac{1}{Vs}} \cdot \left\lbrack \frac{{{\ln \left( {1 - {vr}_{M}} \right)} + {vr}_{M} + \mu}{\cdot {vr}_{M}^{2}}}{{vr}_{M}^{1/3} - {{vr}_{M}/2}} \right\rbrack}\quad {wherein}}}{{vr}_{M} = \frac{1 - \varphi}{X_{M} - \varphi}}} & (A) \end{matrix}$

wherein X_(M) is the degree of change before and after toluene swelling (volume after toluene swelling/volume before toluene swelling)after treatment in a lithium aluminum hydride saturated tetrahydrofuran/toluene (ratio by volume 1/1) mixed solution, φ is the volume percentage of the reinforcing filler in the rubber composition, V_(s) is the molecular volume of toluene, μ is the rubber•toluene interaction coefficient, and vrM is the volume percentage of rubber in the swelled rubber after treatment in a lithium aluminum hydride saturated tetrahydrofuran/toluene (ratio by volume 1/1) mixed solution, a value V[D+M] is obtained from the degree of change before and after toluene swelling of the vulcanized rubber composition treated in a propane-2-thiol (0.4 mol/l)/piperidine (0.4 mol/l) added tetrahydrofuran/toluene (ratio by volume 1/1) mixed solution using the formula (D): $\begin{matrix} \begin{matrix} {{V\left\lbrack {D + M} \right\rbrack} = {{- \frac{1}{Vs}} \cdot \left\lbrack \frac{{\ln \left( {1 - {vr}_{D + M}} \right)} + {vr}_{D + M} + {\mu \cdot {vr}_{D + M}^{2}}}{{vr}_{D + M}^{1/3} - {{vr}_{D + M}/2}} \right\rbrack}} \\ {{{wherein}\quad {vr}_{D + M}} = \frac{1 - \varphi}{x_{D + M} - \varphi}} \end{matrix} & (D) \end{matrix}$

wherein X_(D+M) is the degree of change before and after toluene swelling (volume after toluene swelling/volume before toluene swelling)after treatment in a propane-2-thiol (0.4 mol/l)/piperidine (0.4 mol/l) added tetrahydrofuran/toluene (ratio by volume 1/1) mixed solution, φ, Vs, μ, and vr_(M) are as defined above, and vr_(D+M) is the volume percentage of rubber in the swelled rubber after treatment in a propane-2-thiol (0.4 mol/l)/piperidine (0.4 mol/l) added tetrahydrofuran/toluene (ratio by volume 1/1) mixed solution, and a value VT is obtained from the degree of change before and after toluene swelling of the untreated vulcanized rubber composition using formula (C): $\begin{matrix} \begin{matrix} {{VT} = {{- \frac{1}{Vs}} \cdot \left\lbrack \frac{{\ln \left( {1 - {vr}_{T}} \right)} + {vr}_{T} + {\mu \cdot {vr}_{T}^{2}}}{{vr}_{T}^{1/3} - {{vr}_{T}/2}} \right\rbrack}} \\ {{{wherein}\quad {vr}_{T}} = \frac{1 - \varphi}{X_{T} - \varphi}} \end{matrix} & (C) \end{matrix}$

wherein XT is the degree of change before and after toluene swelling when untreated (volume after toluene swelling/volume before toluene swelling) and vr_(T) is the volume percentage of rubber in the swelled rubber when untreated are such that VM/VT is not more than 0.3 and (VT−V[D+M])/VT is at least 0.4 and further are such that the ratio VM/VD of VD(=V[D+M]−VM) and VM is at least 0.4 and wherein the rate of retention of the tensile strength at break and the elongation at break of the vulcanized rubber composition before and after heat aging at 100° C. for 96 hours is at least 0.7.
 9. A rubber composition as claimed in claim 8, wherein the Mooney viscosity of the starting sulfur compound is not more than
 100. 10. A rubber composition as claimed in claim 8, wherein the sulfur compound is a polysulfide polymer having a number average molecular weight of 200 to
 15000. 11. A rubber composition as claimed in claim 8, wherein the sulfur compound is a polysulfide polymer having the formula (III) to which sulfur is added in the backbone and having y of 3 to 5 on average and z of 3 to 5 on average: R³S_(z)R²(S_(y)R²)_(m)S_(z)R³  (III) wherein, R² is a C₂ to C₁₀ oxyalkylene group and/or a C₂ to C₁₀ and O₂ to C₁₀ polyoxyalkylene group, R³ is at least one functional group selected from the group consisting of a C₁ to C₃₀ hydrocarbon group, y is a number of 1.0 to 6.0, z is a number of 1 to 6, and m is an integer of 1 to 50 wherein the polysulfide polymer has an R² of formula (III) shown by the following formula (IV): —C₂H₄OC_(m′)H_(2m′)OC₂H₄—  (IV) wherein, m′ is an integer of 1 to
 2. 12. A rubber composition as claimed in claim 8, wherein at least one vulcanization accelerator selected from the group consisting of a thiazole base, sulfenamide base, thiuram base, and dithio acid salt base accelerator is compounded in an amount of 0.3 to 5 parts by weight based upon 100 parts by weight of the vulcanizable rubber.
 13. A rubber composition as claimed in claim 8, wherein at least one vulcanization accelerator selected from the group consisting of a guanidine base, thiourea base, aldehyde-ammonia base, and aldehyde-amine base accelerator is compounded in an amount of 0.05 to 1 part by weight based upon 100 parts by weight of the vulcanizable rubber.
 14. A rubber composition-as claimed in claim 8, wherein N-(cyclohexylthio) phthalimide is compounded in an amount of 0.05 to 1 part by weight based upon 100 parts by weight of the vulcanizable rubber.
 15. A rubber composition as claimed in claim 8, wherein 10 to 60 parts by weight of the 100 parts by weight of the vulcanizable rubber are polybutadiene rubber.
 16. A rubber composition as claimed in claim 8, wherein the amount of the reinforcing filler is 40 to 100 parts by weight, including 10 to 40 parts by weight of silica, based upon 100 parts by weight of the vulcanizable rubber and wherein a silane coupling agent is compounded in an amount of 1 to 20% by weight of the amount of silica.
 17. A rubber composition comprising 100 parts by weight of a vulcanizable rubber, a reinforcing filler, and a sulfur compound (1) having the formula (I): —(S_(x)R¹)_(n)—  (I) wherein R¹ represents an organic group, x is an average number of 3 to 5, and n is an integer of 1 to 100 and sulfur (2) in a ratio (1)/(2) of the sulfur compound (1) and the sulfur (2) of less than 0.5 and in a total weight of (1)+(2) of not more than 20 parts by weight.
 18. A rubber composition as claimed in claim 17, wherein the Mooney viscosity of the starting sulfur compound is not more than
 100. 19. A rubber composition as claimed in claim 17, wherein the sulfur compound is a polysulfide polymer having a number average molecular weight of 200 to
 15000. 20. A rubber composition as claimed in claim 17, wherein the sulfur compound is a polysulfide polymer having the formula (III) to which sulfur is added in the backbone and having y of 3 to 5 on average and z of 3 to 5 on average: R³S_(z)R²(S_(y)R²)_(m)S_(z)R³—  (III) wherein R² is a C₂ to C₁₀ oxyalkylene group and/or a C₂ to C₁₀ and O₂ to O₁₀ polyoxyalkylene group, R³ is at least one type of functional group selected from the group consisting of a C₁ to C₃₀ hydrocarbon group, y is a number of 1.0 to 6.0, z is a number of 1 to 6, and m is an integer of 1 to 50, and wherein the polysulfide polymer has an R² of formula (III) shown by the following formula (IV): —C₂H₄OC_(m′)H_(2m′)OC₂H₄—  (IV) wherein m′ is an integer of 1 to
 2. 21. A rubber composition as claimed in claim 17, wherein at least one vulcanization accelerator selected from the group consisting of a thiazole base, sulfenamide base, thiuram base, and dithio acid salt base accelerators is compounded in an amount of 0.3 to 3 parts by weight.
 22. A rubber composition as claimed in claim 17, wherein at least one vulcanization accelerator selected from the group consisting of a guanidine base, aldehyde-ammonia base, aldehyde-amine base, and thiourea base accelerators is compounded in an amount of 0.05 to 1 part by weight based upon 100 parts by weight of vulcanizable rubber.
 23. A rubber composition for a heavy duty tire tread comprising 100 parts by weight of a diene rubber, 40 to 85 parts by weight of a reinforcing filler, 1 to 10 parts by weight of at least one resin selected from the group consisting of a rosin base resin, a cyclopentane diene base resin, and mixtures thereof, a sulfur compound having formula (I) or (II): —(S_(x)R¹)_(n)—  (I) wherein R¹ indicates an organic group, x is an integer of 3 to 5, and n is an integer of 1 to 100

wherein n′ is an integer of 3 or 4 and, optionally, sulfur or a sulfur donor.
 24. A rubber composition for a heavy duty tire tread as claimed in claim 23, wherein the weight of the sulfur compound or the total weight of the sulfur compound and the sulfur or sulfur donor is 0.5 to 3 parts by weight in terms of an effective sulfur based upon 100 parts by weight of the diene rubber.
 25. A rubber composition for a heavy duty tire tread as claimed in claim 23, further comprising a guanidine base vulcanization accelerator compounded in an amount of 0.01 to 1.5 parts by weight based upon 100 parts by weight of diene rubber.
 26. A rubber composition for a heavy duty tire tread as claimed in claim 23, wherein the sulfur compound having formula (I) is a polysulfide polymer having a molecular weight of 200 to
 15000. 27. A rubber composition for a heavy duty tire tread as claimed in claim 23, wherein the sulfur compound having formula (I) is a polysulfide polymer having the formula (III): R³S_(z)R²(S_(y)R²)_(m)S_(z)R³  (III) wherein R² is a C₂ to C₁₀ oxyalkylene group and/or a C₂ to C₁₀ and O₂ to O₁₀ polyoxyalkylene group, R³ is at least one functional group selected from the group consisting of C₁ to C₃₀ hydrocarbon groups, y is a number from 2.0 to 5.0, and m is an integer of 1 to 50 to which sulfur is added in the backbone and in which y is more than 3 but up to 5 on average and z is 1 to 5, wherein an R² of formula (III) the following formula (IV): —C₂H₄OC_(m′)H_(2m′)OC₂H₄—  (IV) wherein, m′ is an integer of 1 to
 2. 